LNP™ COLORCOMP™ Compound W1000Z
- Chemical Family
- Polyesters
SABIC's Specialties Business LNP COLORCOMP W1000I compound is based on Polybutylene Terephthalate (PBT) resin. Added features of this grade include: High Viscosity suitable for Extrusion. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Polyesters & Copolyesters
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polybutylene Terephthalate (PBT)
- Processing Methods
- Compounding, Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Surface Appearance
- High Viscosity
- No Added PFAS
- Unreinforced
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Compounding
- Extrusion
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 51 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 300 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 82 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 117 | — | ASTM D785 |
Table 2 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.31 | — | ASTM D792 |
| Specific Volume ¹¹ | 0.76 | cm³/g | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.08 | % | ASTM D570 |
| Mold Shrinkage (flow, 0.75-2.3 mm) ᵍ ¹¹ | 0.9 - 1.6 | % | SABIC method |
| Mold Shrinkage (flow, 2.3-4.6 mm) ᵍ ¹¹ | 1.5 - 2.3 | % | SABIC method |
| Mold Shrinkage (xflow, 0.75-2.3 mm) ᵍ ¹¹ | 1 - 1.7 | % | SABIC method |
| Mold Shrinkage (xflow, 2.3-4.6 mm) ᵍ ¹¹ | 1.6 - 2.4 | % | SABIC method |
| Melt Volume Rate (at 250°C, 2.16 kg) ¹¹ | 9 | cm³/10 min | ASTM D1238 |
| Melt Volume Rate (at 250°C, 2.16 kg) ¹¹ | 9 | cm³/10 min | ISO 1133 |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 154 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 54 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000081 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 60°C to 138°C, flow) ¹¹ | 0.00014 | 1/°C | ASTM E831 |
Table 4 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 4.E+16 | Ω.cm | ASTM D257 |
Table 5 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1602 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 53 | J/m | ASTM D256 |
| Modified Gardner (at 23°C) ¹¹ | 40 | J | ASTM D3029 |
Table 6 of 6
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 240 - 275 | °C |
| Barrel - Zone 1 Temperature | 200 - 230 | °C |
| Barrel - Zone 2 Temperature | 240 - 255 | °C |
| Barrel - Zone 3 Temperature | 240 - 275 | °C |
| Barrel - Zone 4 Temperature | 240 - 275 | °C |
| Die Temperature | 240 - 275 | °C |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | Hrs |
| Drying Time (Cumulative) | 8 | Hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 245 - 260 | °C |
| Water Bath Temperature | 25 - 35 | °C |