LNP™ COLORCOMP™ Compound NX06514
SABIC's Specialties Business LNP COLORCOMP NX06514 is an unfilled Polycarbonate+ABS resin. Added feature of this material are: non-chlorinated, non-brominated flame retardant with UL V0 & 5VB flame rating, improved heat resistance, balanced flow and impact. This grade is an excellent candidate for a wide variety of applications including appliances, lighting and electrical. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Density
- 1220.0 - 1220.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2700.0 - 2700.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ¹ Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 5VB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Additives Included
- Flame Retardant
- Lubricant (Unspecified)
- Material Features
- Flame Retardant
- Good Aesthetics
- Good Surface Appearance
- Heat Resistance
- Lubricated
- No Added PFAS
- Non-brominated
- Non-chlorinated
Technical data
Table 1 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 40 | % | ASTM D638 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 102 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2650 | MPa | ASTM D790 |
| Hardness (Rockwell R) ¹¹ | 123 | — | ASTM D785 |
| Hardness (Rockwell R) ¹¹ | 123 | — | ISO 2039-2 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 54 | mg/1000cy | ASTM D1044 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 60 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | min. 50 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2800 | MPa | ISO 527 |
Table 2 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.22 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.6 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.4 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 10 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.22 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.2 | % | ISO 62 |
| Melt Volume Rate (at 260°C, 2.16 kg) ¹¹ | 12 | cm³/10 min | ISO 1133 |
Table 3 of 7
21 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 110 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 112 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 90 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 104 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 95 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000072 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000072 | 1/°C | ASTM D696 |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ASTM C177 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000075 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000075 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Table 4 of 7
24 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1.E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+17 | Ω.cm | ASTM D257 |
| Surface Resistivity ¹¹ | min. 1.E+16 | Ω | ASTM D257 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 19.4 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) ¹¹ | 3 | — | ASTM D150 |
| Relative Permittivity (100 Hz) ¹¹ | 3 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.004 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.005 | — | ASTM D150 |
| Dissipation Factor (at 100 Hz) ¹¹ | 0.0049 | — | ASTM D150 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
Table 5 of 7
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 534 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 160 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 61 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy (at -30°C) ¹¹ | 54 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 44 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 14 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 45 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Table 6 of 7
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ¹ | 80 - 90 | °C |
| Drying Time ¹ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ¹ | 8 | Hrs |
| Maximum Moisture Content ¹ | 0.04 | % |
| Melt Temperature ¹ | 245 - 275 | °C |
| Nozzle Temperature ¹ | 245 - 275 | °C |
| Front - Zone 3 Temperature ¹ | 245 - 275 | °C |
| Middle - Zone 2 Temperature ¹ | 220 - 275 | °C |
| Rear - Zone 1 Temperature ¹ | 220 - 255 | °C |
| Mold Temperature ¹ | 60 - 80 | °C |
| Back Pressure ¹ | 0.3 - 0.7 | MPa |
| Screw Speed ¹ | 40 - 70 | rpm |
Table 7 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 2.5 | mm | UL 94 |
| Oxygen Index (LOI) ᵖ | 32 | % | ASTM D2863 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.5 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 2.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 825 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 2 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |