LNP™ COLORCOMP™ Compound R1000SU
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP COLORCOMP R1000SU compound is based on Nylon 6/6 resin. Added features of this grade include: Heat Stabilized, UV Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Flexural Modulus
- 3200.0 - 3200.0 MPa
- Additives Included
- Heat Stabilizer, UV Stabilizer
- Heat Stabilizer
- UV Stabilizer
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением указаны только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных изделий и газовая инжекция.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна применяться в качестве спецификации или использоваться для проектирования деталей или пресс-форм.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Surface Appearance
- Good UV Stability
- Good Weather Stability
- Heat Stabilized
- High Durability
- No Added PFAS
- Plastics and Elastomers End Uses
- Automotive Interior Parts
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Electrical/Electronic Applications
- Home Decors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 75 | MPa | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 10 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3400 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 11 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 3200 | MPa | ISO 178 |
Table 2 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.23 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.22 | g/cm³ | ASTM D792 |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 75 | °C | ISO 75/Af |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 260 - 270 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 265 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 60 - 100 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |