LNP™ COLORCOMP™ Compound NX05467
SABIC's Specialties Business LNP COLORCOMP NX05467 compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend. Added features of this grade is: Non-Chlorinated, Non-Brominated Flame Retardant with UL V0, 5VB and 5VA flame rating.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Density
- 1180.0 - 1180.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2680.0 - 2680.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 5VA
- UL 94 5VB
- UL 94 HB
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Additives Included
- Flame Retardant
- Heat Stabilizer
- Mold Release Agent
- Material Features
- Excellent Aesthetics
- Flame Retardant
- Good Aesthetics
- Good Mold Release
- Good Surface Appearance
- Heat Stabilized
- High Durability
- Non-brominated
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 66 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 50 | % | ASTM D638 |
| Flexural Stress ¹¹ | 103 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 2680 | MPa | ASTM D790 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.18 | — | ASTM D792 |
| Melt Flow Rate (at 260°C, 2.16 kgf) ¹¹ | 17 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Mold Shrinkage (xflow) ᵍ ¹¹ | 0.4 - 0.6 | % | SABIC method |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2 mm, Unannealed) ¹¹ | 87 - 91 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 85 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 85 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 85 | °C | UL 746B |
Table 4 of 6
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | ASTM D257 |
| Surface Resistivity ¹¹ | 1.00E+15 | Ω | ASTM D257 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 890 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 640 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 430 | kV/mm | IEC 60243-1 |
| Relative Permittivity (60 Hz) ¹¹ | 2.8 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.004 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.008 | — | IEC 60250 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 3 | mm | UL 746A |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 90 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 245 - 275 | °C |
| Nozzle Temperature ⁷ | 245 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 245 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 265 | °C |
| Rear - Zone 1 Temperature ⁷ | 220 - 255 | °C |
| Mold Temperature ⁷ | 60 - 80 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.7 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1.2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 2.0 | mm | UL 94 |
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 3.4 | mm | UL 94 |