LNP™ COLORCOMP™ Compound G1000
- Chemical Family
- Polysulfones
SABIC's Specialties Business LNP COLORCOMP G1000 compound is based on unfilled Polysulfone (PSU) resin. Added features of this grade include: Transparent. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polysulfone (PSU)
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Transparent
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Excellent Transparency Properties
- Good Aesthetics
- Good Surface Appearance
- High Durability
- High Temperature Resistance
- No Added PFAS
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.4 | % | ISO 62-1 |
| Specific Gravity ¹¹ | 1.24 | — | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.3 | % | ASTM D570 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.4 - 0.7 | % | SABIC method |
Table 2 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min) ¹¹ | 2500 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5.9 | % | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 60 | MPa | ISO 527 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 76 | MPa | ISO 527 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2500 | MPa | ISO 178 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 115 | MPa | ISO 178 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 70 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 50 - 100 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2480 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 106 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2690 | MPa | ASTM D790 |
Table 3 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 170 | °C | ISO 75/Af |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 183 | °C | ISO 75/Bf |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000061 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000062 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 174 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000056 | 1/°C | ASTM D696 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 160 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 140 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 160 | °C | UL 746B |
Table 4 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 3.00E+17 | Ω.cm | ASTM D257 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0007 | — | ASTM D150 |
| Dissipation Factor (at at 1 kHz) ¹¹ | 0.001 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.006 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 1) ¹¹ | min. 4.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 3) ¹¹ | min. 6 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 4) ¹¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 7 | PLC Code | ASTM D495 |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, at 23°C) ¹¹ | 69 | J/m | ASTM D256 |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 360 - 370 | °C |
| Front - Zone 3 Temperature ⁷ | 350 - 360 | °C |
| Middle - Zone 2 Temperature ⁷ | 340 - 350 | °C |
| Rear - Zone 1 Temperature ⁷ | 325 - 340 | °C |
| Mold Temperature ⁷ | 150 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 4.5 | mm | UL 94 |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |