LNP™ COLORCOMP™ Compound J1000E
- Chemical Family
- Polysulfones
LNP COLORCOMP J1000E compound is based on unfilled Polyethersulfone (PES) resin. Added features of this grade include: Easy Molding.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polyethersulfone (PES)
- Flexural Modulus
- 2800.0 - 2800.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- UL 94 V2
- Technology
- Plastics
- Material Features
- Easy To Mold
- Excellent Aesthetics
- Good Aesthetics
- Good Moldability
- Good Processability
- Good Surface Appearance
- High Durability
- High Temperature Resistance
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 91 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 6.8 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2700 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 136 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2800 | MPa | ISO 178 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.9 | % | SABIC method |
| Density ¹¹ | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.9 | % | ISO 62-1 |
Table 3 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000056 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000057 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 197 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 180 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 170 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 180 | °C | UL 746B |
Table 4 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot Wire Ignition (PLC 3) ¹¹ | min. 0.81 | mm | UL 746A |
| Hot Wire Ignition (PLC 4) ¹¹ | min. 0.43 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 0.43 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 0.81 | mm | UL 746A |
Table 5 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 355 - 370 | °C |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Rear - Zone 1 Temperature ⁷ | 345 - 355 | °C |
| Mold Temperature ⁷ | 140 - 150 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 60 - 100 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.81 | mm | UL 94 |
| UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 0.43 | mm | UL 94 |