LNP™ COLORCOMP™ Compound N1000E
SABIC's Specialties Business LNP COLORCOMP N1000E compound is based on unfilled Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend. Added features of this grade include: Excellent Flow, Impact, High Heat Resistance, Low Temperature Ductility. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Blends & Alloys
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Density
- 1150.0 - 1150.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Additives Included
- Impact Modifier
- Material Features
- Excellent Aesthetics
- Excellent Flow Properties
- Excellent Low Temperature Ductility
- Good Aesthetics
- Good Flow
- Good Processability
- Good Surface Appearance
- High Ductility
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 57 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 100 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2270 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 8.80E+01 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.15 | — | ASTM D792 |
| Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 19 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Table 3 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 130 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 129 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 112 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000072 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Table 4 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.2 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 1.2 | mm | UL 746A |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 587 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 480 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 54 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy (at -30°C) ¹¹ | 54 | J | ASTM D3763 |
Table 6 of 7
15 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Drying Temperature ⁷ | 100 - 110 | °C |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Front - Zone 3 Temperature ⁷ | 260 - 300 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 275 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 255 - 295 | °C |
| Mold Temperature ⁷ | 60 - 90 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 290 | °C |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
| Glow Wire Flammability Index (at 3.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.5 mm) ᵖ | 725 | °C | IEC 60695-2-13 |