LNP™ COLORCOMP™ Compound M1000S
- Chemical Family
- PolyolefinsPolypropylenes (PP)
SABIC's Specialties Business LNP COLORCOMP M1000S compound is based on Polypropylene (PP) resin. Added features of this grade include: Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Melt Flow Index
- 6.0 - 6.0 g/10 min
- Additives Included
Heat Stabilizer, Metal Deactivator, Mold Release Agent; Heat Stabilizer; Metal Deactivator; Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Mold Release
- Good Surface Appearance
- Heat Stabilized
- High Durability
- No Added PFAS
- Unreinforced
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Commercial Appliance
- Consumer Applications
- Containers
- Home Appliances
- Home Decors
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (at 230°C, 2.16 kgf) ¹¹ | 6 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.13 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.12 | g/cm³ | ISO 1183 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.51 - 1.67 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.51 - 1.67 | % | ISO 294 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 28 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 26 | MPa | ISO 527 |
| Tensile Strain (Yield) ¹¹ | 7 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 40 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2160 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 3.00E+01 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 1600 | MPa | ISO 178 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 130 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 94 | °C | ISO 75/Af |
Table 4 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Melt Temperature ⁷ | 215 - 220 | °C |
| Front - Zone 3 Temperature ⁷ | 205 - 215 | °C |
| Middle - Zone 2 Temperature ⁷ | 200 - 210 | °C |
| Rear - Zone 1 Temperature ⁷ | 195 - 205 | °C |
| Mold Temperature ⁷ | 30 - 50 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |