LNP™ COLORCOMP™ Compound DX06407H

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP COLORCOMP DX06407H compound is based on Polycarbonate (PC) resin. Added features of this grade include: Easy Molding, Good Mold Release, Healthcare This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging
Industrial & Transport Packaging

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2290.0 - 2290.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Easy To Mold
Excellent Aesthetics
Good Aesthetics
Good Mold Release
Good Moldability
Good Processability
Good Surface Appearance
High Durability
Plastics and Elastomers End Uses: Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

13 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	63	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	58	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	6.2	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	94	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2340	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2400	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	65	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	54	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	6.3	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	104	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2300	MPa	ISO 527
Flexural Stress ¹¹	91	MPa	ISO 178

Table 2 of 5

6 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.2	—	ASTM D792
Density ¹¹	1.2	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	10.5	g/10 min	ASTM D1238
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	12	cm³/10 min	ISO 1133

Table 3 of 5

4 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	103	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	94	°C	ASTM D648
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	104	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	96	°C	ISO 75/Af

Table 4 of 5