LNP™ COLORCOMP™ Compound DX02663H

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP COLORCOMP DX02663H compound is based on Polycarbonate (PC) resin. Added features of this grade include: High Flow, Good Mold Release and Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging
Industrial & Transport Packaging

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2300.0 - 2300.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: Biocompatible
No Added PFAS
Material Features: Biocompatible
E-Beam Sterilizable
Ethylene Oxide Sterilizable
Excellent Aesthetics
Gamma Sterilizable
Good Aesthetics
Good Mold Release
Good Surface Appearance
Certifications and Compliance: ISO 10993
USP Class VI
Plastics and Elastomers End Uses: Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 8

18 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	65	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	6	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	120	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2370	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	93	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2300	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	70	—	ASTM D785
Hardness (Rockwell R) ¹¹	118	—	ASTM D785
Taber Abrasion (CS-17, 1 kg) ¹¹	10	mg/1000cy	ASTM D1044
Tensile Stress (Yield, 50 mm/min) ¹¹	63	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	50	MPa	ISO 527

Table 2 of 8

10 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.2	—	ASTM D792
Specific Volume ¹¹	0.83	cm³/g	ASTM D792
Density ¹¹	1.2	g/cm³	ISO 1183
Density ¹¹	1.19	g/cm³	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.15	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.35	%	ASTM D570
Water Absorption (Equilibrium, at 100°C) ¹¹	0.58	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	25	g/10 min	ASTM D1238
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	23	cm³/10 min	ISO 1133

Table 3 of 8

12 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	126	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.0000684	1/°C	ASTM E831
Specific Heat ¹¹	1.25	J/g-°C	ASTM C351
Thermal Conductivity ¹¹	0.2	W/m-°C	ISO 8302
Thermal Conductivity ¹¹	0.19	W/m-°C	ASTM C177
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00007	1/°C	ISO 11359-2
Ball Pressure Test (at 123°C to 127°C) ¹¹	Pass	—	IEC 60695-10-2
Vicat Softening Temperature (Rate B/50) ¹¹	139	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	140	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120104, sp=100mm) ¹¹	133	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120104, sp=100mm) ¹¹	121	°C	ISO 75/Ae

Table 4 of 8

13 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	min. 1.E+15	Ω.cm	IEC 60093
Volume Resistivity ¹¹	min. 1.E+17	Ω.cm	ASTM D257
Dielectric Strength (in air, at 3.2mm) ¹¹	14.9	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	2.7	—	IEC 60250
Relative Permittivity (50/60 Hz) ¹¹	3.17	—	ASTM D150
Relative Permittivity (1 MHz) ¹¹	2.7	—	IEC 60250
Relative Permittivity (1 MHz) ¹¹	2.96	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.001	—	IEC 60250
Dissipation Factor (at 50/60 Hz) ¹¹	0.0009	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.01	—	IEC 60250
Dissipation Factor (at at 1 MHz) ¹¹	0.01	—	ASTM D150
Surface Resistivity (ROA) ¹¹	min. 1.E+15	Ω	IEC 60093

Table 5 of 8

3 rows

Characteristic	Value	Unit	Method
Light Transmission (at 2.54 mm) ¹¹	88	%	ASTM D1003
Haze (at 2.54 mm) ¹¹	1	%	ASTM D1003
Refractive Index ¹¹	1.586	—	ASTM D542

Table 6 of 8