LNP™ COLORCOMP™ Compound D1000RFJ
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP COLORCOMP D1000RFJ compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Healthcare, Low Exractable,Food Contact Compliant, Mold Release and UL Rated HB. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Pipes & Plumbing
- Consumer Electronics
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Food & Beverage Packaging
- Healthcare Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ¹² The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Color
- Custom
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Food Contact Acceptable
- Good Aesthetics
- Good Mold Release
- Good Moldability
- Good Surface Appearance
- Heat Stabilized
- High Durability
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Food Packaging
- Home Appliances
- Hoses
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 68 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 125 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 96 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2340 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 70 | — | ASTM D785 |
| Hardness (Rockwell R) ¹¹ | 118 | — | ASTM D785 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 10 | mg/1000cy | ASTM D1044 |
Table 2 of 8
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Specific Volume ¹¹ | 0.83 | cm³/g | ASTM D792 |
| Density ¹¹ | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.15 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ASTM D570 |
| Water Absorption (Equilibrium, at 100°C) ¹¹ | 0.58 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 16 | g/10 min | ASTM D1238 |
Table 3 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) ¹¹ | 154 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 129 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.0000684 | 1/°C | ASTM E831 |
| Specific Heat ¹¹ | 1.25 | J/g-°C | ASTM C351 |
| Thermal Conductivity ¹¹ | 0.19 | W/m-°C | ASTM C177 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Table 4 of 8
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹² | min. 1.E+17 | Ω.cm | ASTM D257 |
| Dielectric Strength (in air, at 3.2mm) ¹² | 14.9 | kV/mm | ASTM D149 |
| Relative Permittivity (50/60 Hz) ¹² | 3.17 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹² | 2.96 | — | ASTM D150 |
| Dissipation Factor (at 50/60 Hz) ¹² | 0.0009 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹² | 0.01 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹² | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 3) ¹² | min. 1.1 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹² | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹² | min. 1.1 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹² | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹² | 2 | PLC Code | UL 746A |
Table 5 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
| Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
| Refractive Index ¹¹ | 1.586 | — | ASTM D542 |
Table 6 of 8
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 3204 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 694 | J/m | ASTM D256 |
| Tensile Impact Strength (Type S) ¹¹ | 546 | kJ/m² | ASTM D1822 |
| Falling Dart Impact (at 23°C) ¹¹ | 169 | J | ASTM D3029 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 62 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 305 | °C |
| Nozzle Temperature ⁷ | 275 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 295 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 8 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.7 | mm | UL 94 |