LNP™ COLORCOMP™ Compound DX00511H

Name: LNP™ COLORCOMP™ Compound DX00511H
Brand: LNP™ COLORCOMP™ Compound

LNP COLORCOMP DX00511H compound is based on Polycarbonate (PC) resin. Added features of this grade include: Good Mold Release and Healthcare.

Product families

Healthcare & Pharma — Medical

Printing & Packaging — Packaging

Plastics — Engineering & Specialty Polymers

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2300.0 - 2300.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Material Features: Excellent Aesthetics
Good Aesthetics
Good Mold Release
Good Surface Appearance
Unreinforced
Plastics and Elastomers End Uses: Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

17 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	68	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	130	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2370	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	97	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2340	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	70	—	ASTM D785
Hardness (Rockwell R) ¹¹	118	—	ASTM D785
Taber Abrasion (CS-17, 1 kg) ¹¹	10	mg/1000cy	ASTM D1044
Tensile Stress (Yield, 50 mm/min) ¹¹	63	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	70	MPa	ISO 527

9 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.2	—	ASTM D792
Specific Volume ¹¹	0.83	cm³/g	ASTM D792
Density ¹¹	1.19	g/cm³	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.15	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.35	%	ASTM D570
Water Absorption (Equilibrium, at 100°C) ¹¹	0.58	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	10.5	g/10 min	ASTM D1238
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	10	cm³/10 min	ISO 1133

14 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	141	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	154	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	132	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.0000684	1/°C	ASTM E831
Specific Heat ¹¹	1.25	J/g-°C	ASTM C351
Thermal Conductivity ¹¹	0.2	W/m-°C	ISO 8302
Thermal Conductivity ¹¹	0.19	W/m-°C	ASTM C177
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00007	1/°C	ISO 11359-2
Ball Pressure Test (at 123°C to 127°C) ¹¹	Pass	—	IEC 60695-10-2
Vicat Softening Temperature (Rate A/50) ¹¹	153	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	142	°C	ISO 306

6 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	min. 1.E+17	Ω.cm	ASTM D257
Dielectric Strength (in air, at 3.2mm) ¹¹	14.9	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	3.17	—	ASTM D150
Relative Permittivity (1 MHz) ¹¹	2.96	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0009	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.01	—	ASTM D150

12 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	3204	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	801	J/m	ASTM D256
Izod Impact (Notched, natural, tints) ¹¹	801	J/m	ASTM D256
Izod Impact (Notched, colors) ¹¹	801	J/m	ASTM D256
Tensile Impact Strength (Type S) ¹¹	577	kJ/m²	ASTM D1822
Falling Dart Impact (at 23°C) ¹¹	169	J	ASTM D3029
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	63	J	ASTM D3763
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80104, at -30°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	10	kJ/m²	ISO 180/1A
Charpy Impact (Notched, at 23°C) ¹¹	35	kJ/m²	ISO 179/2C

14 rows