LNP™ COLORCOMP™ Compound 9X99415

Chemical Family: Polyesters

SABIC's Specialties Business LNP COLORCOMP 9X99415 compound is based on Polyether Block Amide resin. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Product Families

Elastomers — Thermoplastic Elastomers

Thermoplastic Polyester Elastomers (TPE-E)

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Density: 1010.0 - 1010.0 kg/m³
End Uses: Appliances, Automotive Applications, Automotive Interior Parts, Cell Phones, Commercial Appliance, Computer Components, Consumer Applications, Containers, Displays, Electrical/Electronic Applications, Home Appliances, Personal Accessories, Sporting Goods, Surgical Devices, Tablets
Polymer Name: Thermoplastic Polyester Elastomer
Strain at Break: 50.0 - 50.0 %
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Healthcare & Pharma
Personal Care
Printing & Packaging
Technology: Elastomers
Labeling Claims: No Added PFAS
Material Features: Excellent Aesthetics
Good Aesthetics
Good Surface Appearance
No Added PFAS
Unreinforced
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, 50 mm/min) ¹¹	22	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	20	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	min. 50	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	390	MPa	ISO 527
Hardness (Shore D) ¹¹	61	—	ISO 868

Table 2 of 5

5 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.01	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH) ¹¹	1.1	%	ISO 62
Water Absorption (at 23°C, 24hrs) ¹¹	0.7	%	ISO 62-1
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.2	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.5	%	ISO 294

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Melting Temperature ¹¹	172	°C	ISO 11357-3
Vicat Softening Temperature (Rate B/50) ¹¹	164	°C	ISO 306

Table 4 of 5

4 rows

Characteristic	Value	Unit	Method
Charpy Impact (at 23°C, Unnotch Edgew 80104 sp=62mm) ¹¹	No break	kJ/m²	ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80104 sp=62mm) ¹¹	No break	kJ/m²	ISO 179/1eU
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	120	kJ/m²	ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80104 sp=62mm) ¹¹	20	kJ/m²	ISO 179/1eA

Table 5 of 5