LNP™ COLORCOMP™ Compound A1000F
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP COLORCOMP A1000F compound is based on unfilled Acrylonitrile Butadiene Styrene (ABS) resin. Added features of this grade include: Superior Molding. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Melt Flow Index
- 5.6 - 5.6 g/10 min
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Excellent Aesthetics
- Good Aesthetics
- Good Moldability
- Good Processability
- Good Surface Appearance
- No Added PFAS
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate (at 220°C, 10.0 kg) ¹¹ | 18 | g/10 min | ISO 1133 |
| Specific Gravity ¹¹ | 1.04 | — | ASTM D792 |
| Melt Flow Rate (at 230°C, 3.8 kg) ¹¹ | 5.6 | g/10 min | ASTM D1238 |
| Melt Viscosity (at 240°C, 1000 sec⁻¹) ¹¹ | 2250 | Poise | ASTM D3825 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.8 | % | SABIC method |
Table 2 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 47 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 35 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 2.6 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 25 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2370 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 70 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2200 | MPa | ISO 178 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 44 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 33 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 2 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 24 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 2270 | MPa | ASTM D638 |
Table 3 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 81 | °C | ISO 75/Af |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 98 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 99 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 100 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 94 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 80 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000882 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000882 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Comparative Tracking Index (UL, PLC) ᵖ | 0 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 3) ᵖ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 4) ᵖ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ᵖ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate (PLC) ᵖ | 3 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) ᵖ | 6 | PLC Code | ASTM D495 |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 22 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 26 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, at 23°C) ¹¹ | 320 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 30 | J | ASTM D3763 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 95 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 8 | Hrs |
| Maximum Moisture Content ⁷ | 0.1 | % |
| Melt Temperature ⁷ | 220 - 260 | °C |
| Nozzle Temperature ⁷ | 220 - 260 | °C |
| Front - Zone 3 Temperature ⁷ | 215 - 240 | °C |
| Middle - Zone 2 Temperature ⁷ | 205 - 225 | °C |
| Rear - Zone 1 Temperature ⁷ | 190 - 210 | °C |
| Mold Temperature ⁷ | 50 - 70 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |