LNP™ ELCRES™ EXL7414
SABIC's Specialties Business LNP ELCRES EXL7414 is based on Polycarbonate (PC) siloxane copolymer resin. It is a medium flow, non-chlorinated, non-brominated flame retardant opaque grade. It offers excellent low temperature ductility (-40C), extremely thin wall flame retardant capability with UL94 V0 at 0.6mm, and in combination with excellent processability and release with opportunities for shorter cycle times compared to standard Polycarbonate. It is available in wide range of opaque colors and is an excellent candidate for a wide variety of applications such as the battery cover of fast-charging mobile phones that need to be compliant with IEC62368-1.
Product families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRES
- Polymer Name
- Polycarbonate-Siloxane Copolymer
- Flexural Modulus
- 2130.0 - 2130.0 MPa
- Additives Included
Flame Retardant, Heat Stabilizer, Mold Release Agent; Flame Retardant; Heat Stabilizer; Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 5VB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Quality Standards
- IEC 62368-1
Technical data
Table 1 of 7
16 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 53 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 61 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5.3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 120 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2120 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 88 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2150 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 54 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 61 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5.2 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 120 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2150 | MPa | ISO 527 |
Table 2 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.8 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.4 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 12 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 11 | cm³/10 min | ISO 1133 |
Table 3 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 105 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000077 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000087 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.000088 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.000098 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 123 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 124 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 119 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 108 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 80 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 80 | °C | UL 746B |
Table 4 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1E+16 | Ω.cm | ASTM D257 |
| Surface Resistivity ¹¹ | min. 1E+16 | Ω | ASTM D257 |
| Dielectric Constant (at 1.1 GHz) ¹¹ | 2.87 | — | SABIC method |
| Dielectric Constant (at 1.9 GHz) ¹¹ | 2.81 | — | SABIC method |
| Dielectric Constant (at 5 GHz) ¹¹ | 2.81 | — | SABIC method |
| Dielectric Constant (at 10 GHz) ¹¹ | 2.84 | — | SABIC method |
| Dissipation Factor (at 1.1 GHz) ¹¹ | 0.0064 | — | SABIC method |
| Dissipation Factor (at 1.9 GHz) ¹¹ | 0.006 | — | SABIC method |
| Dissipation Factor (at 5 GHz) ¹¹ | 0.006 | — | SABIC method |
| Dissipation Factor (at 10 GHz) ¹¹ | 0.0061 | — | SABIC method |
Table 5 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 900 | J/m | ASTM D256 |
| Izod Impact (Notched, at 0°C) ¹¹ | 850 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 770 | J/m | ASTM D256 |
| Izod Impact (Notched, at -40°C) ¹¹ | 700 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 69 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy (at -30°C) ¹¹ | 66 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 73 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 65 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 78 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 69 | kJ/m² | ISO 179/1eA |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 110 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 295 - 315 | °C |
| Nozzle Temperature ⁷ | 290 - 310 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 315 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 305 | °C |
| Rear - Zone 1 Temperature ⁷ | 270 - 295 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index (LOI) ᵖ | 38 | % | ISO 4589 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.6 | mm | UL 94 |
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 3.0 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ᵖ | 1 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 850 | °C | IEC 60695-2-13 |