LNP™ KONDUIT™ Compound PX11311
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP KONDUIT PX11311 compound is based on Nylon 6 resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Automotive Lighting
- Glazing & Window Elements
- Interior Fixtures
- Equipment & Parts
- Automotive Electronics
- Consumer Electronics
- Displays
- Industrial Automation
- Lighting
- Medical Devices & Assemblies
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ KONDUIT™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber, Mineral
- Glass Fiber
- Mineral
- Flexural Modulus
- 11000.0 - 11000.0 MPa
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Material Features
- Electrically Insulating
- Electrically Isolative
- Flame Retardant
- Non-brominated
- Non-chlorinated
- Thermally Conductive
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Electronics
- Building Materials
- Cell Phones
- Computer Components
- Construction Applications
- Consumer Applications
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 102 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 52 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.5 | % | ISO 527 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 12500 | MPa | ISO 527 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 7240 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 76 | MPa | ASTM D790 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 164 | MPa | ISO 178 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 9040 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 11000 | MPa | ISO 178 |
| Impact Strength ¹¹ | 5.3 - 18.2 | kJ/m² | ISO R179 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.76 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.74 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.33 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.48 | % | ASTM D955 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.25 | % | SABIC method |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.04 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 10.0 kg) ¹¹ | 49 | cm³/10 min | ISO 1133 |
Table 3 of 7
23 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000308 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000313 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000477 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000459 | 1/°C | ASTM E831 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 199 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, flow) ¹¹ | 0.0000346 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -30°C to 80°C, xflow) ¹¹ | 0.0000604 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.0000372 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 40°C to 120°C, flow) ¹¹ | 0.0000194 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.0000734 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 40°C to 120°C, xflow) ¹¹ | 0.0000695 | 1/°C | ASTM E831 |
| Specific Heat ¹¹ | 1.42 | J/g-°C | ASTM C351 |
Table 4 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | min. 1.E+15 | Ω | ASTM D257 |
| Dielectric Strength (in oil, at 1mm) ¹¹ | min. 10 | kV/mm | ASTM D149 |
| Dielectric Constant (at 1.1 GHz) ¹¹ | 4.74 | — | ASTM ES 7-83 |
| Dissipation Factor (at 1.1 GHz) ¹¹ | 0.0077 | — | ASTM ES 7-83 |
| Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 22 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 183 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 43 | J/m | ASTM D256 |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 270 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 275 | °C |
| Mold Temperature ⁷ | 85 - 100 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 20 - 60 | rpm |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 775 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 850 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1 mm) ᵖ | 960 | °C | IEC 60695-2-12 |