ELASTOSIL® R Plus 4305/70
- Chemical Family
- Silicones
ELASTOSIL® R Plus 4305/70 is a two-component, high-consistency silicone rubber specifically developed for the manufacture of extruded articles. Cured articles made from this addition-curing rubber exhibit excellent transparency and demonstrate good to very good mechanical properties. This fast-curing silicone rubber displays good to very good mechanical properties. The vulcanization reaction is significantly faster compared to peroxide-curing materials, thanks to the addition cure process. Additionally, no peroxide decomposition products are formed during vulcanization.
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® R
- End Uses
Battery Cable, Cables, Ignition Cables, Plugs, Wires
- Features
Excellent Transparency Properties, Fast Curing, Food Contact Acceptable, Good Mechanical Properties, Heat Stabilized, High Consistency, Low Compression Set
- Polymer Name
- Silicone Elastomer
- Tear Strength
- 39.0 - 39.0 kN/m
- Processing Methods
- Extrusion
- Note
Cure conditions: 1.5 parts ELASTOSIL AUX Batch PT 1, 15 min / 165 °C in press, post-cured 4 h / 200 °C for cured properties.
- Markets
- Electrical & Electronics
- Properties
ELASTOSIL® R plus 4305/70 is a fast curing silicone rubber exhibiting good to very good mechanical properties. Thanks to addition cure, the vulcanization reaction is significantly faster compared to peroxide curing materials. No peroxide decomposition products are formed during vulcanization. At service temperatures above approx. 180 °C the addition of heat stabilizers is recommended.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Labeling Claims
- Food Contact Acceptable
- Special Features
- Addition Curing
- Food-contact
- Low compression set
- Two-component
- Additives Included
- Heat Stabilizer
- Material Features
- Excellent Transparency Properties
- Fast Curing
- Food Contact Acceptable
- Good Mechanical Properties
- Heat Stabilized
- High Consistency
- Low Compression Set
Technical data
Table 1 of 2
1 row| Characteristic | Value | Unit |
|---|---|---|
| Pot Life (at 23°C) | 24 | Hours |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 175°C) | 14 | % | DIN ISO 815-1 type B method A |
| Density | 1.18 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 600 | % | ISO 37 Type 1 |
| Rebound Resilience | 56 | % | ISO 4662 |
| Shore Hardness A | 70 | — | DIN ISO 48-4 |
| Tear Strength | 39 | N/mm | ASTM D 624 B |
| Tensile Strength | 9.1 | N/mm² | ISO 37 Type 1 |