ELASTOSIL® R Plus 4366/60
- Chemical Family
- Silicones
ELASTOSIL® R Plus 4366/60 is a high consistency silicone rubber specifically designed for the production of extruded articles. It undergoes addition curing as a two-component system. The cured articles demonstrate excellent transparency and exhibit good to very good mechanical properties. In comparison to ELASTOSIL® R plus 4305/60, post-cured parts made from ELASTOSIL® R Plus 4366/60 experience a reduction in coefficient of friction ranging from 50% to 70%.
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® R
- Features
Excellent Transparency Properties, Fast Curing, Food Contact Acceptable, Good Mechanical Properties, Heat Stabilized, High Consistency, Low Coefficient of Friction
- Polymer Name
- Silicone Elastomer
- Tear Strength
- 41.0 - 41.0 kN/m
- Processing Methods
- Extrusion
- Note
Cure conditions: 2.0 % ELASTOSIL® AUX Batch PT 1, 15 min / 165 °C in press, post-cured 4 h / 200 °C for cured poperties.
- Properties
ELASTOSIL® R plus 4366/60 exhibits a reduced coefficient of friction in comparison with other platinum curing grades (e.g. ELASTOSIL® R plus 4305 series). The vulcanizates are transparent and noted for good to very good mechanical properties.. Thanks to addition cure, the vulcanization reaction is significantly faster compared to peroxide curing materials. No peroxide decomposition products are formed during vulcanization. At service temperatures above approx. 180 °C the addition of heat stabilizers is recommended.
- Cure
- Chemical Cure
- Applications
- Dairy Applications
- Profiles & Tubings
- Technology
- Elastomers
- Labeling Claims
- Food Contact Acceptable
- Special Features
- Addition Curing
- Food-contact
- Low coefficient of friction
- Two-component
- Additives Included
- Heat Stabilizer
- Material Features
- Excellent Transparency Properties
- Fast Curing
- Food Contact Acceptable
- Good Mechanical Properties
- Heat Stabilized
- High Consistency
- Low Coefficient of Friction
- Storage Information
Please store the cardboard boxes in a dry and cool place. Once opened, cardboard boxes should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulfur or phosphorus compounds.
Technical data
Table 1 of 2
1 row| Characteristic | Value | Unit |
|---|---|---|
| Pot Life (at 23°C) | 24 | Hours |
Table 2 of 2
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (at 22 hours, 175°C) | 20 | % | DIN ISO 815-1 type B method A |
| Density | 1.15 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break) | 550 | % | ISO 37 Type 1 |
| Rebound Resilience | 56 | % | ISO 4662 |
| Shore Hardness A | 60 | — | DIN ISO 48-4 |
| Tear Strength | 41 | N/mm | ASTM D 624 B |
| Tensile Strength | 7.6 | N/mm² | ISO 37 Type 1 |