ELASTOSIL® R 865/60 S
- Chemical Family
- Silicones
ELASTOSIL® R 865/60 S provides a wide range of functional advantages. This material guarantees superior rebound resilience and minimal compression set. It can be easily pigmented using ELASTOSIL® PT Pigment Pastes and exhibits favorable processing characteristics. The various grades available, including ELASTOSIL® R 865/40 to ELASTOSIL® R 865/70, can be blended in any proportion to achieve intermediate hardness levels.
Properties
- Physical Form
- Liquid
- Paste
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® R
- End Uses
- Automotive Components
- Features
Excellent Rebound, Food Contact Acceptable, Good Processability, High Consistency, High Resilience, Low Compression Set, Pigmentable
- Polymer Name
- Silicone Elastomer
- Tear Strength
- 18.0 - 18.0 kN/m
- Processing Methods
- Calendering, Extrusion
- Note
Cure conditions: 0.5 % ELASTOSIL® AUX Crosslinker C6 (45 % paste of 2,5-bis-(t-butylperoxy)-2,5-dimethyl hexane in silicone rubber), 15 min / 165 °C in press, post-cured 4 h / 200 °C for cured properties.
- Color
- Transparent
- Applications
- Calendered Sheets
- Dairy Applications
- General Automotive Parts
- Molded Parts
- Technology
- Elastomers
- Labeling Claims
- Food Contact Acceptable
- Special Features
- Food-contact
- High rebound resilience
- Ultra-low compression set
- Material Features
- Excellent Rebound
- Food Contact Acceptable
- Good Processability
- High Consistency
- High Resilience
- Low Compression Set
- Pigmentable
- Storage Information
Please store the cardboard boxes in a dry and cool place. Already opened boxes should be closed again to avoid any contamination.
- Chemical Inventories
- AIIC (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- PICCS (Phillipines)
- TCSI (Taiwan)
- TSCA (USA)
Technical data
Table 1 of 1
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (Curing Agent C6, at 22 hours, 175°C) | 5 | % | DIN ISO 815-1 type B method A |
| Density (Curing Agent C6) | 1.16 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Curing Agent C6) | 380 | % | ISO 37 Type 1 |
| Rebound Resilience (Curing Agent C6) | 57 | % | ISO 4662 |
| Shore Hardness A (Curing Agent C6) | 60 | — | DIN ISO 48-4 |
| Tear Strength (Curing Agent C6) | 18 | N/mm | ASTM D 624 B |
| Tensile Strength (Curing Agent C6) | 9.3 | N/mm² | ISO 37 Type 1 |