ELASTOSIL® R 401/30 S
- Chemical Family
- Silicones
ELASTOSIL® R 401/30 S is a high-consistency silicone rubber (HCR). Vulcanizates cured with peroxide made from this compound exhibit a unique combination of characteristics. It is noted for its good flexibility, high transparency, and mechanical properties. The compound is easily pigmented with ELASTOSIL® Color Paste PT and has good processing characteristics.
Product families
- Silicone Elastomers
Other characteristics
- Brand
- ELASTOSIL® R
- End Uses
Exhaust Duct Systems, Gaskets, General Purpose, Profiles, Tubes, Tubing, Vibration Dampers
- Features
Excellent Transparency Properties, Food Contact Acceptable, General Purpose, Good Mechanical Properties, Good Processability, Heat Stabilized, High Consistency, High Flexibility, Pigmentable
- Polymer Name
- Silicone Elastomer
- Tear Strength
- 22.0 - 22.0 kN/m
- Processing Methods
- Calendering, Extrusion
- Markets
- Building & Construction
- Industrial
- Properties
This product can be used within a temperature range of - 55°C to + 210 °C. The addition of heat stabilizers at service temperatures of more than 180°C is recommended.
- Cure
- Chemical Cure
- Technology
- Elastomers
- Labeling Claims
- Food Contact Acceptable
- Additives Included
- Heat Stabilizer
- Material Features
- Excellent Transparency Properties
- Food Contact Acceptable
- General Purpose
- Good Mechanical Properties
- Good Processability
- Heat Stabilized
- High Consistency
- High Flexibility
- Storage Information
Please store the cardboard boxes in a dry and cool place. Already opened boxes should be closed again to avoid any contamination.
- Chemical Inventories
- AICS (Australia)
- DSL (Canada)
- ENCS (Japan)
- IECSC (China)
- PICCS (Phillipines)
- TCSI (Taiwan)
- TSCA (USA)
Technical data
Table 1 of 1
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Compression Set (Curing Agent C1, at 22 hours, 175°C) | 15 | % | DIN ISO 815-1 type B method A |
| Compression Set (Curing Agent E, at 22 hours, 175°C) | 20 | % | DIN ISO 815-1 type B method A |
| Density (Curing Agent C1) | 1.09 | g/cm³ | DIN EN ISO 1183-1 A |
| Density (Curing Agent E) | 1.09 | g/cm³ | DIN EN ISO 1183-1 A |
| Elongation (at break, Curing Agent C1) | 800 | % | ISO 37 Type 1 |
| Elongation (at break, Curing Agent E) | 720 | % | ISO 37 Type 1 |
| Rebound Resilience (Curing Agent C1) | 48 | % | ISO 4662 |
| Rebound Resilience (Curing Agent E) | 59 | % | ISO 4662 |
| Shore Hardness A (Curing Agent C1) | 33 | — | DIN ISO 48-4 |
| Shore Hardness A (Curing Agent E) | 34 | — | DIN ISO 48-4 |
| Tear Strength (Curing Agent C1) | 24 | N/mm | ASTM D 624 B |
| Tear Strength (Curing Agent E) | 22 | N/mm | ASTM D 624 B |