Indestructible Paint IP7420 Range 2Pk Epoxy Dry Film Lubricant
- Chemical Family
- Epoxy & Epoxy Derivatives
IP7420 Range 2Pk Epoxy Dry Film Lubricant is a 2-part air drying PTFE loaded epoxy finish used to provide an abrasion and wear-resistant coating. The Dry finish is resistant to abrasion, corrosion and most vehicle operating fluids and chemical attack from brake fluid.
Product families
Applications
- Aerospace Fluids & Lubricants
Product Families
- Lubricants & Oils
Other characteristics
- Features
Abrasion Resistant, Corrosion Resistant, Wear Resistant
- Product Type
- Dry Lubricants
- Application Area
- Brakes
- Markets
- Automotive & Transportation
- Storage
Highly flammable liquid - Store and use in accordance with flammable liquid regulations.; Shelf Life - 12 months temperate; 6 months tropical
- Pack Size
- 1 liter
- 5 liter
- Components
IP7420 - Base (Part A); IP7420 - CAT (Part B); IP9064 - Thin (may be added if required for coating complex unit geometry)
- Application
IP7420 coatings can be applied directly to the metal of composite substrates or used over a suitable primer system. Suitable Primers are IP9064-6362 Chromate Primer and IP9064-6500 Non-chromate Primer. For Composite applications, it is recommended that the adhesion of IP7420 is tested before use.; Ensure that all surfaces are clean and free from dirt.; Paint Mixing – the IP7420 requires mixing before use. Mix the Part A component and then add to the Part B. The coating can be mixed by add in A to B or B to A depending upon the volume required and available measuring vessels.; Mixing Instructions - Refer to product range listings and label on the base component. The Part A+B mix requires thorough stirring before use. A minimum of 2 minutes per liter of product is recommended.; Thinner/Reducer Addition - 665-550-025 Thinner; Apply by spray. Small areas can be applied by brush.; Air Dry Touch Dry - 2 - 3 hours Hard Dry - 16 - 24 hours; Touch Dry - 2 - 3 hours; Hard Dry - 16 - 24 hours; If you can flash off for 15 minutes and the force cure for 30 minutes at 105°C - 125°C.; Heat Cure Flash Off - 20 - 30 minutes Cure - 30 minutes at 105°C - 125°C.; Flash Off - 20 - 30 minutes; Cure - 30 minutes at 105°C - 125°C.
- Cure
- Air Dry
- Performance
Tested as a system with IP9064-6362 Primer on Magnesium, Aluminum and Steel to the following minimum specification:; Resistant to 100 hours in salt-water fog; Resistant to 100 hours dry heat at 180°C; Resistant to 100 hours at 150°C in lubricating oil; Resistant to 100 hours at 180°C in dry heat; Resistant to 100 hours with engine fuel
- Technology
- Ready-to-Use Products
- Cleanup Solvents
- 40006 or 665-550-025
- Approvals/Specifications
Complies with the Environmental Resistance and Chemical.; Resistance criteria of: Def Stan 80-161
- Ready to Use Product Features
- Abrasion Resistant
- Corrosion Resistant
- Wear Resistant
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Supply Viscosity (21°C - 25°C) | 70 - 100 | s | ISO5 |
| Flash Point | 25.0 | °C | — |
| VOC Content | 400 - 480 | g/l | — |
| Density | 1.2 - 1.4 | kg/l | — |
| Catalyst | IP7420-CAT | — | — |
| Theoretical Coverage (25 Micron) | 15.0 | m²/l | — |