LNP™ THERMOCOMP™ Compound DF006ERH
- Chemical Family
- Polycarbonate (PC)
SABIC's Specialties Business LNP THERMOCOMP DF006ERH is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Healthcare, Easy Molding, Mold Release. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Electronics
- Displays
- Medical Devices & Assemblies
- Connectors
- Housings & Enclosures
- Switches & Relays
- Aerospace & Aviation
Product Families
- Polycarbonates
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 7800.0 - 7800.0 MPa
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Easy To Mold
- Good Mold Release
- Good Moldability
- Good Processability
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Aerospace Applications
- Automotive Applications
- Cell Phones
- Computer Components
- Displays
- Electrical Components
- Electrical Enclosure
- Electrical Internal Frame
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 132 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.7 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 9500 | MPa | ASTM D638 |
| Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 190 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 8400 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 125 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.2 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 9000 | MPa | ISO 527 |
| Flexural Strength (at 2 mm/min) ¹¹ | 185 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7800 | MPa | ISO 178 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.42 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.42 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.11 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.48 | % | ISO 294 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 136 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 140 | °C | ISO 75/Af |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 865 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 133 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 8 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 4 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 60 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 305 - 325 | °C |
| Front - Zone 3 Temperature ⁷ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ⁷ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 295 - 305 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |