LNP™ THERMOCOMP™ Compound RF006L

Chemical Family: Polyamides

LNP THERMOCOMP RF006L compound is based on Nylon 6/6 resin containing 30% glass fiber. Added features of this grade include: Low Extractables.

Product families

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Printing & Packaging — Packaging

Food & Beverage Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber
Flexural Modulus: 8730.0 - 8730.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Printing & Packaging
Technology: Plastics
Labeling Claims: Food Contact Acceptable
Material Features: Cost Effective
Food Contact Acceptable
Good Mold Release
High Impact Resistance
High Modulus
High Stiffness
Low Extractables
Low Leachable
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Building Materials
Consumer Applications
Electrical Enclosure
Electrical Internal Frame
Food Packaging
Home Appliances
Hoses
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	157	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.4	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	10540	MPa	ASTM D638
Flexural Stress ¹¹	220	MPa	ASTM D790
Flexural Modulus ¹¹	8730	MPa	ASTM D790

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.59	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4	%	ASTM D955

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	246	°C	ASTM D648