LNP™ THERMOCOMP™ Compound ZFM3314M

Name: LNP™ THERMOCOMP™ Compound ZFM3314M
Brand: LNP™ THERMOCOMP™ Compound

SABIC's Specialties Business LNP THERMOCOMP ZFM3314M compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 20% glass fiber and minerals. Added features of this grade include: Non-Brominated & Non-Chlorinated Flame Retardant, Impact Modified, Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Density: 1250.0 - 1250.0 kg/m³
Polymer Name: PPO/PS Alloy
Flexural Modulus: 5800.0 - 5800.0 MPa
Processing Methods: Injection Molding
Note: ⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Labeling Claims: Bromine-free
Chlorine-free
No Added PFAS
Fillers Included: Glass Fiber
Mica
Mineral
Additives Included: Flame Retardant
Heat Stabilizer
Impact Modifier
Material Features: Cost Effective
Flame Retardant
Heat Stabilized
High Stiffness
Impact Modified
Low Warpage
No Added PFAS
Non-brominated
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	95	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6100	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	145	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5800	MPa	ISO 178

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.25	g/cm³	ISO 1183
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	17	cm³/10 min	ISO 1133

Table 3 of 5

4 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000032	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000062	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	179	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	170	°C	ISO 75/Af

Table 4 of 5