LNP™ THERMOCOMP™ Compound IF006L
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP IF006L compound is based on Nylon 6/12 resin containing 30% glass fiber. Added features of this grade include: Low Extractables. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Pipes & Plumbing
- Consumer Electronics
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Housings & Enclosures
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 612 (PA 612)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 7790.0 - 7790.0 MPa
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литья, литье крупных деталей, литье тонкостенных изделий и газовое литье.; ¹¹ Информация, указанная в технических паспортах, должна использоваться только для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.; ᵖ Рейтинги UL, указанные в техническом паспорте, могут не охватывать весь диапазон толщин и цветов. Для получения подробной информации, пожалуйста, обратитесь к желтой карточке UL.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Cost Effective
- Food Contact Acceptable
- Good Mold Release
- High Modulus
- High Stiffness
- Low Extractables
- Low Leachable
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Consumer Applications
- Electrical Enclosure
- Electrical Internal Frame
- Food Packaging
- Home Appliances
- Hoses
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 135 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 3 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 8750 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 206 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 7790 | MPa | ASTM D790 |
Table 2 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.31 | g/cm³ | ASTM D792 |
Table 3 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 198 | °C | ASTM D648 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 587 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 85 | J/m | ASTM D256 |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.12 - 0.2 | % |
| Melt Temperature ⁷ | 270 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 280 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 270 | °C |
| Rear - Zone 1 Temperature ⁷ | 255 - 265 | °C |
| Mold Temperature ⁷ | 65 - 95 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |