LNP™ THERMOCOMP™ Compound EX00781H
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business LNP THERMOCOMP EX00781H is a compound is based on Polyetherimide (PEI) resin containing 20% glass fiber. Added features of this grade include: Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Medical Devices & Assemblies
- Surgical Instruments & Trays
- Healthcare Packaging
- Industrial & Transport Packaging
- Housings & Enclosures
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 3310.0 - 3310.0 MPa
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Electrical & Electronics
- Healthcare & Pharma
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- High Modulus
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Electrical Enclosure
- Electrical Internal Frame
- Internal Armature
- Medical Devices
- Medical Packaging
- Medical/Healthcare Applications
- Pharmaceutical Packaging
- Surgical Devices
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 91 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 90 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 5.9 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5.3 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 3320 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 145 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3150 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 91 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 89 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 5.4 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3250 | MPa | ISO 527 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.31 | — | ASTM D792 |
| Melt Flow Rate (at 337°C, 6.6 kgf) ¹¹ | 12.3 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 340°C, 5.0 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
Table 3 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 189 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 213 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 189 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 37 | J/m | ASTM D256 |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
Table 5 of 5
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 360 - 400 | °C |
| Rear - Zone 1 Temperature ⁷ | 360 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 370 - 390 | °C |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Nozzle Temperature ⁷ | 390 - 400 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed (Circumferential speed) ⁷ | 0.2 - 0.3 | m/s |
| Vent Depth ⁷ | 0.025 - 0.076 | mm |