LNP™ THERMOCOMP™ Compound EC008APQ
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business LNP™ THERMOCOMP™ EC008APQ compound is based on Polyetherimide (PEI) resin containing 40% carbon fiber. Added features of this grade include: Electrically Conductive, High Flow. FAR25.853 Compliant.
Product families
Applications
- Consumer Goods — Sports & Recreation
- Powertrain & UTH
- Glazing & Window Elements
- Interior Fixtures
- Connectors
- Housings & Enclosures
- Switches & Relays
- Aerospace & Aviation
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 30560.0 - 30560.0 MPa
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Quality Standards
- FAR 25.853
- Material Features
- Cost Effective
- Electrically Conductive
- Flame Retardant
- High Flow
- High Flowability
- High Stiffness
- High Strength
- High Temperature Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Aerospace Applications
- Automotive Applications
- Automotive Under The Hood
- Building Materials
- Construction Applications
- Consumer Applications
- Electrical Components
- Electrical Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 268 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 39420 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 356 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 31300 | MPa | ASTM D790 |
| Hardness (Rockwell M) ¹¹ | 112 | — | ASTM D785 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 247 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 0.9 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 35480 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 364 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 30560 | MPa | ISO 178 |
| Compressive Strength ¹¹ | 218 | MPa | SABIC method |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.44 | — | ASTM D792 |
| Density ¹¹ | 1.433 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.11 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.1 - 0.5 | % | ASTM D955 |
| Melt Flow Rate (at 380°C, 6.7 kgf) ¹¹ | 40 | g/10 min | ASTM D1238 |
| Poisson's Ratio ¹¹ | 0.44 | — | ASTM E132 |
Table 3 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 193 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, flow) ¹¹ | 0.000003 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) ¹¹ | 0.00004 | 1/°C | ASTM E831 |
Table 4 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | 4100 | Ω.cm | ASTM D257 |
| Surface Resistivity ¹¹ | 450 | Ω | ASTM D257 |
Table 5 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 560 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 64 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 7 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 33 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 6 of 6
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 360 - 400 | °C |
| Rear - Zone 1 Temperature ⁷ | 360 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 370 - 390 | °C |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Nozzle Temperature ⁷ | 390 - 400 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed (Circumferential speed) ⁷ | 0.2 - 0.3 | m/s |
| Vent Depth ⁷ | 0.025 - 0.076 | mm |