LNP™ THERMOCOMP™ Compound UF0067W
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP UF0067W compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Hot Water Moldable, Non-Brominated & Non-Chlorinated Flame Retardant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Powertrain & UTH
- Consumer Electronics
- Displays
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 9130.0 - 9130.0 MPa
- Additives Included
Flame Retardant, Heat Stabilizer, Mold Release Agent; Flame Retardant; Heat Stabilizer; Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 V0
- UL 94 V1
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- No Added PFAS
- Material Features
- Cost Effective
- Flame Retardant
- Good Mold Release
- Heat Stabilized
- High Modulus
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Under The Hood
- Cell Phones
- Commercial Appliance
- Computer Components
- Displays
- Electrical Components
- Electrical Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 143 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.5 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 10540 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 213 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 10200 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 128 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.9 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 11310 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 189 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 9130 | MPa | ISO 178 |
Table 2 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.2 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.5 | % | ISO 294 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.2 - 1.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.2 - 1.5 | % | ISO 294 |
Table 3 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 299 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 281 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000234 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000025 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000504 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000511 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 277 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 125 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 50 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 125 | °C | UL 746B |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 29.7 | kV/mm | ASTM D149 |
| Relative Permittivity (1 kHz) ¹¹ | 4.05 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 3.82 | — | ASTM D150 |
| Dissipation Factor (at at 1 kHz) ¹¹ | 0.0115 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.0128 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
Table 5 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 662 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 6.40E+01 | J/m | ASTM D256 |
| Multi-Axial Impact ¹¹ | 1 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 32 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 - 110 | °C |
| Drying Time ⁷ | 3 - 5 | Hrs |
| Melt Temperature ⁷ | 280 - 320 | °C |
| Nozzle Temperature ⁷ | 280 - 320 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 320 | °C |
| Middle - Zone 2 Temperature ⁷ | 280 - 320 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 280 | °C |
| Mold Temperature ⁷ | 90 - 120 | °C |
| Back Pressure ⁷ | 1 - 5 | MPa |
| Screw Speed ⁷ | 30 - 100 | rpm |
Table 7 of 7
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-1 Flame Class Rating) ᵖ | min. 1 | mm | UL 94 |