SiliXan® M 150
- CASE Ingredients Features
- Abrasion ResistanceChemical ResistanceExcellent Scratch ResistanceImproves Adhesion
- Chemical Family
- Silica
SiliXan® M 150 is methacrylate modified polymer based on SiO2 / ZrO2 used as unsaturated binder for the formulation of scratch resistant UV coatings. Additive for commercial acrylate- or methacrylate based coating formulations, inks or binder. This binder is preferably used for UV-curing formulation, but also use for peroxidic thermal curing is possible.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
- Other Resins & Binders
Other characteristics
- Brand
- SiliXan
- End Uses
- Radiation Curable Coating
- Features
Abrasion Resistance, Chemical Resistance, Excellent Scratch Resistance, Improves Adhesion
- Compatible Substrates & Surfaces
- Metal
- Markets
- Paints & Coatings
- Printing & Packaging
- Properties
Excellent abrasion resistance high chemical resistance easy-to-clean-properties good antistaining properties improved adhesion on metal
- Application
SiliXan M 150 is both UV and thermal curing:; UV- curing: a mercury lamp with a total irradiation dosage from 2-3 J/cm2; thermal curing: the system will be cured by IR or heat; The drying speed depends on the coating formulation and the type and content of used photo- or thermoinitiator.
- Cure
- Heat Cure
- Radiation Cure
- Applications
Paints & Coatings — Other Paints & Coatings Applications; Printing & Packaging — Other Printing & Packaging Applications
- Coating Type
- Radiation Curable Coating
- Technology
- CASE Ingredients
- Packaging Type
- Cans
- Drums
- Compatible Substrates and Surfaces
- Metal
Technical data
Table 1 of 1
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Apha colour | 350 - 400 | — | DIN ISO 6271 |
| Viscosity at 23°C | 1330 ± 335 | mPa*s | ISO 2555 (L4, 200 U/min) |
| Solid content (1g/1h 150°C) | 91.2 ± 1 | % | solid bulk scale |
| Water content | 3.34 | % | ISO 760 |
| Density at 23°C | 1.18 | g/ml | DIN 12791 ISO 649 |
| Flash point | 110 | °C | DIN ISO 3679 |
| Content of double bonds | 2.0 ± 0.1 | mol/kg | — |
| SiO2 / ZrO2 relation | 40 : 1 | mol | — |