SiliXan® U 100
- CASE Ingredients Features
- Abrasion ResistanceGood Chemical StabilityUV Stability
- Chemical Family
- Polyurethanes (PU)
SiliXan® U 100 is urethane compound with silicon alkoxy groups used as binder for formulation of high quality UV stable clearcoats or pigmented coatings. Cobinder to improve the abrasion resistance, and film hardness of solvent-based polyurethane, epoxy, melamine or silicone resin systems.
Properties
- Physical Form
- Liquid
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
- Other Resins & Binders
Other characteristics
- Brand
- SiliXan
- End Uses
- Clearcoat, Enamel, Solventborne Coating
- Features
Abrasion Resistance, Good Chemical Stability, UV Stability
- Compatible Substrates & Surfaces
- Aluminum, Metal
- Markets
- Paints & Coatings
- Storage
The shelf life of the product is 6 months, provided the original container is stored tightly closed at +15 to +25°C. Opened containers should be processed shortly. The expiry date of each batch appears on the product label. Storage beyond the indicated period does not necessarily mean that the product is useless. However, in this case a review of the properties for the respective application is essential for reasons of quality assurance.
- PACKAGING
- 5L can
- 30L drum
- 200L drum
- Applications
Paints & Coatings — Other Paints & Coatings Applications
- Coating Type
- Clearcoat
- Enamel
- Solventborne Coating
- Technology
- CASE Ingredients
- Packaging Type
- Cans
- Drums
- Labeling Claims
- Isocyanates-free
- Solvent-free
- Technical Details
Drying conditions:; This raw material contains no isocyanate, hydroxy, carboxy or epoxy groups. Reactive groups of SiliXan U 100 are silicon alkoxy groups, which can be cured to Si-O-Si-bonds with tailor-made crosslinking catalysts (SiliXan® Cat) or with standard additives such as blocked acids, amines, compounds of Ti or Zr. The material can either be cured at room temperature with moistue or accelerated at temperatures between 40 ° C and 200 °C or shortly at 250 °C.; Solubility / thinnability :; SiliXan U 100 can be thinned with esters, ether esters, alcohols, xylene and toluene. The storage stability of the respective solutions must be tested. The raw material is unsoluble in water and in benzine. The solvents should have a water content <0,1%. Traces of water can lead to unwanted condensation reaction of slicon alkoxy groups.; Compatibility :; SiliXan U 100 is miscible with the usual coating raw materials such as resins and binders based on isocyanates, polyester or acrylate polyols, silicone or melamine types. The compatibility with other types of binder must be checked in particular cases.
- Compatible Polymers and Resins
- Epoxies (EP)
- Polyurethanes (PU)
- Compatible Substrates and Surfaces
- Aluminum
- Metal
Technical data
Table 1 of 1
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Apha color | 10 - 15 | — | DIN ISO 6271 |
| Viscosity at 23°C | 315 ± 50 | mPa*s | ISO 2555 (L2, 60 U/min) |
| Solid content (1g/1h 150°C) | 95 ± 2 | % | solid bulk scale |
| Water content | ≤ 0.1 | % | ISO 760 |
| Flash Point | min. 95 | °C | DIN ISO 3679 |
| Density at 23°C | 1.12 | g/ml | DIN 12791 ISO 649 |