LNP™ THERMOCOMP™ Compound EC006E
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
LNP THERMOCOMP EC006E compound is based on Polyetherimide (PEI) resin containing 30% carbon fiber. Added features of this grade include: Easy Molding, Electrically Conductive.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 19160.0 - 19160.0 MPa
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Cost Effective
- ESD Protection
- Easy To Mold
- Electrically Conductive
- Good Moldability
- Good Processability
- High Stiffness
- High Strength
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Doors
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 230 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹¹ | 215 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 1.3 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 1.5 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 23300 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 314 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 306 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 19160 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 20800 | MPa | ISO 178 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 18470 | MPa | ISO 527 |
Table 2 of 5
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.39 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.394 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.17 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.1 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.51 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 | % | ASTM D955 |
| Wear Factor Washer ¹¹ | 75 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF ¹¹ | 0.52 | — | ASTM D3702 Modified: Manual |
| Static COF ¹¹ | 0.48 | — | ASTM D3702 Modified: Manual |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.25 | % | ISO 62 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 206 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 208 | °C | ISO 75/Af |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 6 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 34 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 5 of 5
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 360 - 400 | °C |
| Rear - Zone 1 Temperature ⁷ | 360 - 380 | °C |
| Middle - Zone 2 Temperature ⁷ | 370 - 390 | °C |
| Front - Zone 3 Temperature ⁷ | 380 - 400 | °C |
| Nozzle Temperature ⁷ | 390 - 400 | °C |
| Mold Temperature ⁷ | 140 - 180 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed (Circumferential speed) ⁷ | 0.2 - 0.3 | m/s |
| Vent Depth ⁷ | 0.025 - 0.076 | mm |