LNP™ THERMOCOMP™ Compound RFZ349XC

Chemical Family: Polyamides

SABIC's Specialties Business LNP™ THERMOCOMP™ RFZ349XC compound is based on Nylon 6/6 resin containing 20% glass fiber, 15% milled glass. Added features of this grade include: Flame Retardant.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Lawn & Garden
Consumer Goods — Sports & Recreation

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyamide 66 (PA 66)
Fillers Included: Glass Fiber, Milled Glass Fiber
Glass Fiber
Milled Glass Fiber
Flexural Modulus: 7170.0 - 7170.0 MPa
Additives Included: Flame Retardant, Mold Release Agent
Flame Retardant
Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Technology: Plastics
Material Features: Cost Effective
Flame Retardant
Good Mold Release
High Stiffness
Low Warpage
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Building Materials
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	85	MPa	ISO 527
Tensile Stress (Break) ¹¹	124	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.3	%	ASTM D638
Tensile Strain (Break) ¹¹	3.2	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	11030	MPa	ASTM D638
Flexural Stress ¹¹	179	MPa	ASTM D790
Flexural Stress ¹¹	197	MPa	ISO 178
Flexural Modulus ¹¹	9000	MPa	ISO 178
Flexural Modulus ¹¹	7170	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	11400	MPa	ISO 527

Table 2 of 5

7 rows

Characteristic	Value	Unit	Method
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.2	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.39	%	ISO 294
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.19	%	ISO 294
Density ¹¹	1.66	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.43	%	ISO 62

Table 3 of 5

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	237	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	235	°C	ISO 75/Af

Table 4 of 5

6 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	587	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	64	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	7	J	ASTM D3763
Multi-Axial Impact ¹¹	2	J	ISO 6603
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	39	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Table 5 of 5