LNP™ THERMOCOMP™ Compound LC006EXQ

Chemical Family: Polyether Ether Ketone (PEEK)

LNP THERMOCOMP LC006EXQ compound is based on Polyetheretherketone (PEEK) resin containing 30% carbon fiber. Added features of this grade include: Electrically Conductive, Easy Molding.

Product families

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays
Industrial Automation

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyetheretherketone (PEEK)
Fillers Included: Carbon Fiber
Flexural Modulus: 27230.0 - 27230.0 MPa
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Consumer Goods
Electrical & Electronics
Industrial
Technology: Plastics
Material Features: Cost Effective
Easy To Mold
Electrically Conductive
Good Moldability
Good Processability
High Stiffness
High Strength
High Temperature Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Cell Phones
Computer Components
Displays
Electrical Components
Electrical Enclosure
Electrical Internal Frame
Electrical/Electronic Applications
Industrial Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

12 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	314	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	31700	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	477	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	27100	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	319	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.5	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	35320	MPa	ISO 527
Flexural Stress ¹¹	457	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	27230	MPa	ISO 178
Shear Modulus ¹¹	4756	MPa	ASTM D732
Shear Strength ¹¹	119	MPa	ASTM D732

Table 2 of 6

5 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.4	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.05	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.15 - 0.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 1.4	%	ASTM D955
Poisson's Ratio ¹¹	0.44	—	ASTM E132

Table 3 of 6

3 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	332	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 150°C, flow) ¹¹	0.000005	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) ¹¹	0.00003	1/°C	ASTM E831

Table 4 of 6

1 row

Characteristic	Value	Unit	Method
Surface Resistivity ¹¹	1000 - 10000	Ω	ASTM D257

Table 5 of 6