BJB Enterprises TC-1607-AB
- Chemical Family
- Epoxy & Epoxy Derivatives
BJB Enterprises TC-1607-AB is an unfilled, medium viscosity laminating resin for high temperature plastic tooling and part fabrication. This system is ideal for wet lay-up tooling applications where excellentdimensional stability and high mechanical properties are required.
Properties
- Physical Form
- Liquid
Product families
Applications
- Industrial — Other Industrial Applications
- Other Industrial Applications
Product Families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Note
Physical Properties : With 8 plies of 7500-glass cloth, vacuum bagged.
- Usage
- Easy to use for lay-ups requiring vacuum bagging
- Withstands temperatures to 350°F (177°C)
- Designed for fabrication of a variety of molds
- Markets
- Industrial
- Storage
Store at ambient temperatures, 65-80ºF (18-27ºC). Unopened containers will have a shelf life of 12months from date of shipment when properly stored at recommended temperatures. Purge opened containers with dry nitrogen before re-sealing.
- Appearance
- Translucent Amber
- Cure
- Heat Cure
- Technology
- Plastics
- Safty Precaution
Use in a well-ventilated area. Avoid contact with skin using protective gloves and protective clothing. Repeated or prolonged contact on the skin may cause an allergic reaction. Eye protection is extremely important. Alwaysuse approved safety glasses or goggles when handling this product.
- Application
All physical property results are based upon post-curing this system. The following procedure provides the best results:; 1)150 ° F (66 ° C) for 1.5 to 2 hours; 2)250 ° F (121 ° C) for 2 hours; 3)300 ° F (149 ° C) for 1 hour; 4)350 ° F (177 ° C) for 1 hour; Allow to cool in the oven. This procedure provides further stabilization and eliminates possible thermal shocks for cavity tools that are temporarily clamped together for curing purposes.
- Material Features
- Dimensional Stability
- Good Mechanical Properties
- Medium Viscosity
- Certifications and Compliance
- RoHS Compliant
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Hardness (77°F (25°C)) | 93 - 97 | Shore D |
| Hardness (350°F (177°C)) | 85 - 89 | Shore D |
| Density | 1.16 | g/cc |
| Tensile Strength | 25500 | psi |
| Flexural Strength (77°F (25°C)) | 48600 | psi |
| Flexural Strength (350°F (177°C)) | 15000 | psi |
| Flexural Strength (350°F (177°C)) | 1 x 106 | psi |
| Flexural Strength (350°F (177°C)) | 1 x 10⁶ | psi |
| Flexural Modulus (77°F (25°C)) | 2.25 x 10⁶ | psi |
| Shrinkage (16 plies of 7500-fiberglass cloth laid up at 0° and 45°) | 0.0013 | in/in |
| Compressive Strength | 26400 | psi |
| Coefficient of Thermal Expansion | 0.8 x 10⁻⁵ | in/in/°F |
Table 2 of 2
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio by weight (Part A) | 100 | — | — |
| Mix Ratio by volume (Part A) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.2 | — | — |
| Color (Part A) | Pale Yellow | — | — |
| Viscosity (77°F (25°C), Part A) | 6500 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 2100 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 35 minutes | — | — |
| Demold Time (77°F (25°C)) | 24 hours | — | — |
| Mix Ratio by weight (Part B) | 100 | — | — |
| Mix Ratio by volume (Part B) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 1.2 | — | — |
| Color (Part B) | Pale Yellow | — | — |