To catalogue
BJB Enterprises TC-1601-AB
- Chemical Family
- Epoxy & Epoxy Derivatives
BJB Enterprises TC-1601-AB is an unfilled, low viscosity laminating epoxy resin for variety of fabricating applications. It features the ability tocure at room temperature for applications that do not require a working service temperature above 180°F (82°C). When post cured at elevated temperatures, this system can provide service up to 300°F (149°C).TC-1601is commonly used to reinforce fiberglass, Kevlar/aramid, and carbon fiber fabrics. It is alsoused as an adhesive for bonding wood, composites, and other substrates. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for filets, fairings, and bonding applications.
Properties
- Physical Form
- Liquid
Product families
Applications
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
Industrial — Leather & Textiles
- Textile Manufacturing
Product Families
Plastics — Thermoset Resins
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 275.79 - 275.79 MPa
- Markets
- Adhesives & Sealants
- Industrial
- Appearance
- Clear Pale Yellow
- Cure
- Air Dry
- Technology
- Plastics
- Packaging Type
- Drums
- Material Features
- General Purpose
- Good Adhesion
- Low Viscosity
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness (77°F (25°C)) | 93 - 97 | Shore D | ASTM D2240 |
| Density | 1.17 | g/cc | ASTM D792 |
| Cubic | 24.7 | Inches per Pound | — |
| Tensile Strength | 35000 | psi | ASTM D638 |
| Flexural Strength | 40000 | psi | ASTM D790 |
| Flexural Modulus | 2.3 x 10⁶ | psi | ASTM D790 |
| Shrinkage Linear | 0.00015 | in/in | — |
| Izod Impact, notched | 5 | ft-lb/in | ASTM D256 |
| Heat Deflection Temperature (66 psi) | 250 (121) | °F(°C) | ASTM D648 |
| Compressive Strength | 42000 | psi | ASTM D695 |
| Water Absorption (100 hours) | 1.5 | % | ASTM D570 |
| Coefficient of Thermal Expansion | 1.1 x 10⁻⁵ | in/in/°F | ASTM D3386 |
Table 2 of 2
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio by weight (Part A) | 100 | — | — |
| Mix Ratio by volume (Part A) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.15 | — | — |
| Color (Part A) | Colorless | — | — |
| Viscosity (77°F (25°C), Part A) | 2000 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 1700 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 60 minutes | — | — |
| Demold Time (77°F (25°C)) | 16 - 24 hours | — | — |
| Mix Ratio by weight (Part B) | 20 | — | — |
| Mix Ratio by volume (Part B) | 24 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 0.98 | — | — |
| Color (Part B) | Amber | — | — |