BJB Enterprises MD-60 REV 1 A/B
- Chemical Family
- Polyurethanes (PU)
BJB Enterprises MD-60 REV 1 A/B is a series of semi rigid, medium work time urethane elastomers exhibit great flexibility and excellent durability. These tough, abrasion resistant systems easily process at room temperature.The MD Series is perfect for larger or more complex parts and offers superior performance in many applications such as rollers, foundry tooling and high impact semi rigid parts. For faster work times consider BJB’s FD Series of elastomers.
Properties
- Physical Form
- Liquid
Product families
Applications
- Industrial — Other Industrial Applications
- Other Industrial Applications
Product Families
- Polyurethane Rubbers
Other characteristics
- Features
Abrasion Resistant, Durable, Excellent Flexibility, Good Processability, Good Tear Strength, Good Toughness, High Performance, High Tensile Strength, Semi Rigid
- Polymer Name
- Polyurethane Thermoset Elastomer (unspecified)
- Note
*Note: Reported physical properties are based on test specimens cured 1-3 hours at room temperature then 16 hours at 160°F (71°C).. +Shrink test specimens are cured for 24 hours at room temperature and then 16 hours at 160°F (71°C).
- Markets
- Industrial
- Storage
Store ambient temperatures, 65-80°F (18-27°C). Unopened containers will have a shelf life of 6monthsfrom dateof shipment when properly stored at recommendedtemperatures. Purge opened containers with dry nitrogen before re-sealing.
- Appearance
- Clear Amber
- Technology
- Elastomers
- Packaging Type
- Drums
- Safty Precaution
Use in a well-ventilated area. Avoid contact with skin using protective gloves and protective clothing. Repeated or prolonged contact on the skin may cause an allergic reaction. Eye protectionis extremely important. Always use approved safety glasses or goggles when handling this product.
- Application
Most of the physical properties can be achieved in 5-7 days at 77°F (25°C). You may use your own post-cure schedule but the physical properties may vary from BJB's cureschedule of 1-3 hours at 77°F (25°C) followed by16 hours at 160°F (71°C). Do not exceed curing temperature of 200°F (93°C).; When MD-60REV 1A/B is used to produce molds or parts from plaster, wood or other porous substrates, we would first recommend that they besealed.Release agents may then be applied over the sealed surface.; BJB offers silicone RTV mold making materials along with a wide range of accessory items. These include de-airing agents, pigments, mold releases, and Jiffy®Mixers. Visit BJB's website at www.bjbenterprises.com or consult a BJB representative for more information.
- Material Features
- Abrasion Resistant
- Durable
- Excellent Flexibility
- Good Processability
- Good Tear Strength
- Good Toughness
- High Performance
- High Tensile Strength
- HIGHLIGHTS
- RoHS/REACH compliant
- 2:1 user friendly ratio
- High tensile and tear strength
- Molds and cast parts
- Cures at room temperature
- Certifications and Compliance
- RoHS Compliant
Technical data
Table 1 of 2
22 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness (Elevated Temperature Cure*) | 55 - 65 | Shore D | ASTM D2240-04e1 |
| Density (Elevated Temperature Cure*) | 1.147 | g/cc | ASTM D792-00 |
| Cubic (Elevated Temperature Cure*) | 25.09 | Inches per Pound | — |
| Tensile Strength (Elevated Temperature Cure*) | 4700 | psi | ASTM D412-98a(2002)e1 |
| Tensile Modulus (Elevated Temperature Cure*) | 45000 | psi | ASTM D412-98a(2002)e1 |
| Elongation (Elevated Temperature Cure*) | 450 | % | ASTM D412-98a(2002)e1 |
| Tear Strength (Elevated Temperature Cure*) | 475 | pli | ASTM D624-00e1 |
| Shrinkage Linear (Elevated Temperature Cure*) | TBD | in/in | ASTM D2566 (1” depth) |
| Izod Impact notched (Elevated Temperature Cure*) | min. 16 | ft-lb/in | ASTM D256-05 |
| Dielectric Constant (1 MHz, Elevated Temperature Cure*) | 4.659 | — | ASTM D150-87 |
| Dissipation Factor (1 MHz, Elevated Temperature Cure*) | 0.047 | — | ASTM D150-87 |
| Hardness (7 Day Ambient Cure) | 55 - 65 | Shore D | ASTM D2240-04e1 |
Table 2 of 2
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Gel Time | 15 - 20 minutes | — | — |
| Mix Ratio by weight (Part A) | 100 | — | — |
| Mix Ratio by volume (Part A) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.103 | — | — |
| Color (Part A) | Pale Yellow | — | — |
| Viscosity (77°F (25°C), Part A) | 4500 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 2800 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 10 - 15 minutes | — | — |
| Demold Time (77°F (25°C)) | 2 - 3 hours | — | — |
| Mix Ratio by weight (Part B) | 50 | — | — |
| Mix Ratio by volume (Part B) | 50 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 1.111 | — | — |