BJB Enterprises TC-1614-AB is an unfilled, low viscosity epoxy resin system.It is designed to seal porous to semi-porous substrates developing remarkable strength.TC-1614-AB also has exceptional adhesive characteristics and is capable of high temperatures.
Properties
- Physical Form
- Liquid
Product families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 86.87 - 86.87 MPa
- Note
Reported physical properties based on elevated temperature cured test specimens.
- Usage
Easy to use and apply; Withstands temperatures up to350ºF(177°C); Penetrates and seals porous surfaces with excellent adhesion; Can be pigmented for color enhancement; Works great for sealing 3D Printed parts; Recommended by several 3D Printer Manufacturers
- Markets
- Adhesives & Sealants
- Industrial
- Storage
Store at ambient temperatures, 65-80ºF (18-27ºC). Unopened containers will have a shelf life of 12months from date of shipment when properly stored at recommended temperatures. Purge opened containers with dry nitrogen before re-sealing.
- Appearance
- Yellow Opaque
- Cure
- Heat Cure
- Applications
Adhesives & Sealants — Other Adhesives & Sealants Applications; Industrial — Other Industrial Applications
- Technology
- Plastics
- Safty Precaution
Use in a well-ventilated area. Avoid contact with skin using protective gloves and protective clothing. Repeated or prolonged contact on the skin may cause an allergic reaction. Eye protection is extremely important. Always use approved safety glasses or goggles when handling this product.
- Application
All physical property results are based upon post-curing this system. The following procedure provides the best results:; 150F (66C) for 1.5 to 2 hours; 250F (121C) for 2hours; 300F (149C) for 1 hour; 350F (177C) for 1 hour; Allow to cool in the oven. This procedure provides further stabilization and eliminates possible thermal shocks for cavity tools that are temporarily clamped together for curing purposes
- Material Features
- Ease of Handling
- Excellent Strength
- Good Adhesion
- Good Sealant Properties
- Low Viscosity
- Thermal Shock Resistant
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 83 - 87 | Shore D | ASTM D2240 |
| Density | 1.14 | g/cc | ASTM D792 |
| Cubic | 25.1 | Inches per Pound | — |
| Tensile Strength | 9500 | psi | ASTM D638 |
| Tensile Modulus | 320000 | psi | ASTM D638 |
| Elongation | 5 | % | ASTM D638 |
| Flexural Strength | 12600 | psi | ASTM D790 |
| Flexural Modulus | 380000 | psi | ASTM D790 |
| Shrinkage Linear (12”x ½” x ½”) | 0.008 | in/in | — |
| Izod Impact, notched | 0.44 | ft-lb/in | ASTM D256 |
Table 2 of 2
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio by weight (Part A) | 100 | — | — |
| Mix Ratio by volume (Part A) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.13 | — | — |
| Color (Part A) | Colorless | — | — |
| Viscosity (77°F (25°C), Part A) | 550 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 600 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 2 hours | — | — |
| Tack Free (77°F (25°C), 5 hours ) | 10 - 12 hours | — | — |
| Tack Free (120°F (48.9°C)) | 5 hours | — | — |
| Mix Ratio by weight (Part B) | 20 | — | — |
| Mix Ratio by volume (Part B) | 23 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 0.98 | — | — |