BJB Enterprises TC-1600-AB
- Chemical Family
- Epoxy & Epoxy Derivatives
BJB Enterprises TC-1600-AB is an unfilled, low viscosity laminating epoxy resin for variety of fabricating applications. It features the ability to cure at room temperature for applications that do not require a working service temperature above 180°F (82 °C). When post cured at elevated temperatures, this system can provide service up to 300°F (149°C). TC-1600 is commonly used to reinforce fiberglass, Kevlar/aramid, and carbon fiber fabrics. It is also used as an adhesive for bonding wood, composites, and other substrates. Adding fillers like fumed silica, micro-spheres, and short-strand fibers can create pastes for filets, fairings, and bonding applications.
Properties
- Physical Form
- Liquid
Product families
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications
- Textile Manufacturing
Product Families
- Epoxies
Other characteristics
- Polymer Name
- Epoxy Resins & Compounds
- Flexural Strength
- 275.79 - 275.79 MPa
- Markets
- Adhesives & Sealants
- Industrial
- Storage
Store at ambient temperatures, 65-80ºF (18-27ºC). Unopened containers will have a shelf life of 12 months from date of shipment when properly stored at recommended temperatures. Purge opened containers with dry nitrogen before re-sealing.
- Appearance
- Clear
- Cure
- Air Dry
- Technology
- Plastics
- Safty Precaution
Use in a well-ventilated area. Avoid contact with skin using protective gloves and protective clothing. Repeated or prolonged contact on the skin may cause an allergic reaction. Eye protection is extremely important. Always use approved safety glasses or goggles when handling this product.
- Application
TC-1600 A/B may need to be post cured when parts or tools will be subject to service temperatures in excess of 180°F (82°C), or after laminating in cold weather conditions. Generally, most laminates can be de-molded at room temperature after 12-15 hours. Post-curing will expedite demold time, however a laminate should always be allowed to cool to room temperature before demolding.; 1) 77°F (25°C) - 16-24 hours [Will provide service to 180°F (82°C)]; 2) 150°F (66°C) - 2 hours followed by step #3; 3) 250°F (121°C) - 1 hour [Will provide service to 300°F (149°C)]; TC-1601 A/B may need to be post cured when parts or tools will be subject to service temperatures in excess of 180°F (82°C), or after laminating in cold weather conditions. Generally, most laminates can be de-molded at room temperature after 12-15 hours. Post-curing will expedite demold time, however a laminate should always be allowed to cool to room temperature before demolding.
- Material Features
- General Purpose
- Good Adhesion
- Low Viscosity
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 95 | Shore D | ASTM D2240 |
| Density | 1.17 | g/cc | ASTM D792 |
| Cubic | 24.7 | Inches per Pound | — |
| Tensile Strength | 35000 | psi | ASTM D638 |
| Flexural Strength | 40000 | psi | ASTM D790 |
| Flexural Modulus | 2.3 x 10⁶ | psi | ASTM D790 |
| Shrinkage | 0.00015 | in/in | — |
| Izod Impact, notched | 5 | ft-lb/in | ASTM D256 |
| Heat Deflection Temperature (66 psi) | 250 (121) | °F(°C) | ASTM D648 |
| Compressive Strength | 42000 | psi | ASTM D695 |
| Water Absorption (100 hours) | 1.5 | % | ASTM D570 |
| Coefficient of Thermal Expansion | 1.1 x 10⁻⁵ | in/in/°F | ASTM D3386 |
Table 2 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio by weight (Part A) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.15 | — | — |
| Viscosity (77°F (25°C), Part A) | 2000 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 1700 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 30 minutes | — | — |
| Cure Schedule | 12 - 15 hours | — | — |
| Mix Ratio by weight (Part B) | 20 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 0.98 | — | — |
| Viscosity (77°F (25°C), Part B) | 185 | — | — |