BJB Enterprises WC-565-AB
- Chemical Family
- Polyurethanes (PU)
BJB Enterprises WC-565-AB is a two-part, clear, colorless aliphatic-based polyurethane elastomer. It is recommended for use whenever a flexible, permanently transparent elastomer is required. Itis UV light and oxidation resistant and can be easily tinted or pigmented to clean bright colors.WC-565-AB does not contain MOCA, TDI, or MDA. In addition to being an excellent castable product, it also functions well as an adhesive for bonding various substrates.
Properties
- Physical Form
- Liquid
Product families
- Polyurethane Rubbers
Other characteristics
- Features
Good Flexibility, Oxidation Resistant, Resistance to UV lights, Solventless
- Polymer Name
- Polyurethane Thermoset Elastomer (unspecified)
- Processing Methods
- Casting
- Markets
- Adhesives & Sealants
- Industrial
- Storage
Store at ambient temperatures, 65-80ºF (18-27ºC). Unopenedcontainers will have a shelf life of 6 months from date of shipment when properly stored at recommended temperatures. Purge opened containers with dry nitrogen before re-sealing.
- Appearance
- Clear
- Technology
- Elastomers
- Packaging Type
- Drums
- Application
Most of the physical properties can be achieved in 5-7 days at 77ºF (25ºC).You may use your own post-cure schedule but the physical properties may vary from BJB's cure schedule of 1-3 hours at 77ºF (25ºC) followed by 16 hours at 160ºF (71°C). Do not exceed curingtemperatures of 200ºF (93ºC).If you are using heat to acceleratethe demold time, allow the part to cool down to ambient temperature before demolding.
- Material Features
- Good Flexibility
- Oxidation Resistant
- Resistance to UV lights
- Solventless
- Plastics and Elastomers Processing Methods
- Casting
Technical data
Table 1 of 2
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 60 - 70 | Shore A | ASTM D2240-04e1 |
| Density | 1.02 | g/cc | ASTM D792-00 |
| Cubic | 26.54 | Inches per Pound | — |
| Tensile Strength | 753 | psi | ASTM D412-98a(2002)e1 |
| Elongation | 200 | % | ASTM D412-98a(2002)e1 |
| Tear Strength | 59 | pli | ASTM D624-00e1 |
| Shrinkage Linear | 0.004 | in/in | ASTM D2566 (1” depth) |
| Dielectric Constant (1 MHz) | 3.483 | — | ASTM D150-87 |
| Dissipation Factor (1 MHz) | 0.061 | — | ASTM D150-87 |
Table 2 of 2
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mix Ratio by weight (Part A) | 100 | — | — |
| Mix Ratio by volume (Part A) | 95 | — | — |
| Specific Gravity (77°F (25°C), Part A) | 1.07 | — | — |
| Color (Part A) | Colorless | — | — |
| Viscosity (77°F (25°C), Part A) | 4725 | — | Brookfield |
| Mixed Viscosity (77°F (25°C)) | 1100 | cps | Brookfield |
| Work Time (100g mass, 77°F (25°C)) | 15 minutes | — | — |
| Gel Time | 20 minutes | — | — |
| Demold Time (77°F (25°C)) | 6 - 8 hours | — | — |
| Mix Ratio by weight (Part B) | 100 | — | — |
| Mix Ratio by volume (Part B) | 100 | — | — |
| Specific Gravity (77°F (25°C), Part B) | 1.02 | — | — |