EpoxyGrip® 2005
- Chemical Family
- Epoxy & Epoxy Derivatives
EpoxyGrip® 2005 is a high build, direct to metal epoxy to be applied as a one or two oat system for the exterior of tanks. Used on structural steel, steel tanks, offshore platforms, barges, refineries, petrochemical plants, power plants, railcars, pulp & paper mills, masonry surfaces and other areas as recommended. EpoxyGrip 2005 may be used as a surface tolerant single coat system in mild duty applications.
Product families
- Protective Coatings
Other characteristics
- Brand
- EpoxyGrip
- Features
Chemical Resistant, Excellent Substrate Adhesion, Excellent Wetting Behaviour, Extended Recoat Window, Good Adhesion, Low VOC, Medium Gloss, Salt Water/Spray Resistant, Water Resistant; Direct to Metal; Semi-gloss finish; VOC compliant; High Build Formulation; Acceptable for use on UFGS 099713.27; Excellent build on edges; Rapid and extended recoat windows; Single coat capability; Excellent wetting and adhesion properties; Good chemical resistance; 1:1 Mixing Ratio
- Product Type
- 2K (2 component) Coating, Epoxy Coating
- 2K (2 component) Coating
- Epoxy Coating
- Application Area
- Barges, Railcars, Refineries, Tanks
- Barges
- Railcars
- Refineries
- Tanks
- Application Method
- Brush, Roller, Spray
- Compatible Substrates & Surfaces
- Metal, Steel
- Pot Life
Three hours at 75° and less at higher temperatures.
- Topcoats
When additional protection is required, EpoxyGrip 2005 may be topcoated with a urethane such as UreGrip 3000 or VSC1200.
- Resistance
EpoxyGrip 2005 is resistant to a wide range of chemicals in atmospheric exposures. The following is a guide to the proper selection.; NR=Not Recommended
- Shelf LIfe
2 years for both the Part A and B when stored inside at 40°F to 110°F.
- Substrates
EpoxyGrip 2005 is normally applied directly to steel. EpoxyGrip 2005 can be applied to cured ZincGuard 1000, ZincGuard 1500, EpoxyGrip 2100, and MasticGrip 2500. Consult SSPC-PS Guide 8.00 for topcoating zinc-rich primers.
- Technology
- Ready-to-Use Products
- Shipping Data
- Shipping weights (approx.)
- Package unit
- Flash Point: (Setaflash)
- Qualifications
Exceed requirements of SSPC Paint 22 performance requirements.
- Labeling Claims
- Low VOC
- Application Methods
- Brush
- Roller
- Spray
- Film Thickness (Per Coat)
- Dry film thickness
- 8 to 10 mils Wet film thickness: 10 to 12 mils Theoretical coverage: 160 sq. ft. at 8 mils DFT
- Note
- One coat is normally required; however, certain colors may require additional coats for hiding.
- Ready to Use Product Features
- Chemical Resistant
- Excellent Substrate Adhesion
- Excellent Wetting Behaviour
- Extended Recoat Window
- Good Adhesion
- Low VOC
- Medium Gloss
- Salt Water/Spray Resistant
- Compatible Substrates and Surfaces
- Metal
- Steel
Technical data
Table 1 of 2
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Abrasion Resistance (1 kg Load/1000 Cycles) | Weight loss | — | ASTM D 4060 |
| Adhesion | 4031.0 | psi | ASTM D 4541 |
| Continuous Temperature Resistance (Non-immersion) | 250.0 | °F | — |
| Abrasion Resistance (CS 17 Wheel) | 22.0 | mg | ASTM D 4060 |
| Impact Resistance (Direct Impact) | 80.0 | in-lbs. | ASTM D 2794 |
| Non-Continuous Temperature Resistance (Non-Immersion) | 300.0 | °F | — |
| Reducer 1 (1 pint/gal.) | 2.04 | lbs./gal. | — |
| Reducer 2 (1 pint/gal.) | 2.09 | lbs./gal. | — |
| Theoretical Coverage of Mixed Gallon (1 mil) | 1283.0 | sq. ft. | — |
| Theoretical Volume Solids of Mixed Material | 79 - 81 | % | — |
| Volatile Organic Content Unthinned | 1.44 | lbs./gal. | — |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Salt Spray | 1000.0 | Hours | ASTM B 117 |