ATTSHIELD XO
ATTSHIELD XO - Unsaturated isophthalic polyester resin with good mechanical and glass wetting properties. The resin is thixotropic, has been accelerated, and has a low styrene emission system. At normal room temperature, cure with methyl ethyl ketone peroxide (MEKP).
Identification
Product families
Applications
- Equipment & Parts
- Tooling & Moldmaking
- Other Power Water & Utilities Applications
- Marine
Product Families
- Thermoset Resins
- Polyesters
Other characteristics
- Brand
- ATTSHIELD
- Cure Method
- Chemical Cure
- Polymer Name
- Thermoset Polyester
- Processing Methods
- Casting, Spray Lay-up
- Notes
Gel time was determined at 25°C with 1g of PMEK added to 100g of resin. (1) Condition: Thickness 3mm, post curing: 80 C - 6 hours 2) 3 layers of 450 g/m glass mat, 2 layers of 570 g/m roving, 6 hours post curing at 80°C
- Safety
Working with resin for a long time may cause headache or vomiting due to inhalation of styrene fumes. Therefore, work in rooms equipped with supply and exhaust ventilation; In case of contact with skin, wash thoroughly with soap and water; In case of contact with eyes, rinse immediately with plenty ofwater and see a doctor; Full cure does not occur if the catalyst content low (below 0.1%) or low air temperature in the working room.; When working, use chemical protection agents (chemical goggles, mask, gloves, etc.); Do not add metal salts (accelerators) to peroxides (catalysts); Do not add organic peroxides to hot diluent.
- Markets
- Automotive & Transportation
- Industrial
- Storage
Store in a cool, dry place away from heat and sunlight.; Keep containers tightly closed to prevent monomer volatilization and water penetration; It is recommended that the storage temperature not exceed 25°C
- Features
- Good crack resistance
- Low shrinkage
- Appearance
- Reddish Liquid
- Application
Designed for the manufacture of fiberglass products with increased resistance to various mildly aggressive environments by manual molding or spraying. Recommended for the manufacture of water tanks, septic tanks, boats General purpose fiberglass products.
- Cure
- Chemical Cure
- Technology
- Composite Materials
- Plastics
- Packaging Type
- Drums
- Composites End Use
- Marine Applications
- Tanks
- Material Features
- Chemical Resistant
- Excellent Mechanical Strength
- High Strength
- Compatible Reinforcements
- Glass Fiber
- Composite Materials Functions
- Resins Binders & Matrix Materials
- Composites Processing Methods
- Casting
- Spray Lay-up
- Plastics and Elastomers End Uses
- Septic Tanks
- Plastics and Elastomers Functions
- Resin
Technical data
Table 1 of 2
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Barcol Hardness | 45.0 | — |
| Barcol Hardness | 68.0 | — |
| Flexural Strength | 120.0 | MPa |
| Modulus of Elasticity (Bending) | 3.3 | Gpa |
| Tensile Strength (Stretching) | 65.0 | MPa |
| Tensile Strength (Stretching) | 192.0 | MPa |
| Elongation at Break | 2.3 | % |
| Thermal Temperature Deformations | 68.0 | — |
| Tensile Strength (Bend) | 310.0 | MPa |
| Modulus of Elasticity (Bend) | 10.0 | GPa |
| Modulus of Elasticity (Stretching) | 4.1 | GPa |
Table 2 of 2
3 rows| Characteristic | Value | Unit |
|---|---|---|
| Thixotropic Index | 2.0 - 4.0 | — |
| Viscosity (25°C) | 400 - 600 | mPas |
| Gel time (25°C) | 15 - 20 | min |