Ceramabind™ 875
- CASE Ingredients Features
- Air DryingHigh Temperature Performance
Ceramabind™ 875 is an acidic powdered binder system used to formulate high-strength, hydraulic-setting cements for electrical potting or molding applications. A powder blend is typically formulated by adding one part binder to four parts filler by weight. Water is then added in a ratio of 15–20 parts to 100 parts powder blend by weight.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications; Paints & Coatings — Other Paints & Coatings Applications
- Potting Compounds
- Other Specialty Coatings
Product Families
- Other Resins & Binders
Other characteristics
- Brand
- Ceramabind
- Features
- Air Drying, High Temperature Performance
- Curing
Air dry at room temperature for 1 - 2 hours.; Heat cure at 200ºF for 2 - 4 hours.; Final cure at 250ºF for 2 - 4 hours.; This binder can also be set at room temperature in 16 - 24 hours without heat curing.
- Safety
All Ceramabind™ products are water-based materials that can be washed from the skin, in the uncured state, with mild soap and warm water.; Prolonged skin contact should be avoided to prevent irritation.; If any material contacts the eyes, flush continuously with water or neutralizing solutions, then consult a physician immediately.
- Carrier
- Water
- Markets
- Adhesives & Sealants
- Electrical & Electronics
- Paints & Coatings
- Storage
Storage Unopened containers have a six-month shelf life when stored at room temperature.; Make sure opened containers are capped securely to prevent evaporation.; Place a plastic film in between the cap and container to prevent air leakage.; Store containers between 45ºF and 95ºF.
- Cure
- Air Dry
- Heat Cure
- Technology
- CASE Ingredients
- Application and Mixing
Liquid binder-to-powder weight ratios of 4:1 to 1:1 are recommended when formulating adhesives, coatings and pastes.; Powder binder (875) to filler ratio of 1:4 is recommended.; Blend powder slowly into binder until desired viscosity is achieved.; Vacuum degas as required to reduce entrapped air.; Apply the mixture to clean surfaces.; Extremely smooth surfaces are difficult to wet and should be sandblasted, etched, or slightly oxidized wherever possible.; Porous substrates tend to absorb and separate the binder from the powder; these substrates should be pre-coated with the binder only before applying the mixture.
Technical data
Table 1 of 1
4 rows| Characteristic | Value | Unit |
|---|---|---|
| pH Value | 2.8 | — |
| Density | 1.36 | g/cc |
| Solids Content by Weight | 100.0 | % |
| Temperature Resistance | 3000.0 | ºF |