Ceramabind™ 642
Ceramabind™ 642 is a basic solution that is highly compatible with most ceramic and metal powders. Good wettability and tack, and excellent acid resistance after curing. Extremely moisture resistant after a high-temperature cure. Sets up in thick cross-sections when properly formulated.
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Adhesives & Sealants — Other Adhesives & Sealants Applications; Paints & Coatings — Other Paints & Coatings Applications
- Other Specialty Coatings
Product Families
- Other Resins & Binders
Other characteristics
- Brand
- Ceramabind
- Features
Acid Resistance, Air Drying, Excellent Tack Stability, Good Moisture Resistance, Good Wettability, High Temperature Performance
- Compatible Substrates & Surfaces
- Ceramic, Metal
- Curing
- Air dry at room temperature for 1 - 2 hours.
- Heat cure at 200ºF for 1 - 2 hours.
- Heat cure at 350ºF for 1 - 2 hours.
- Final cure at 500ºF for 1 hour.
- Safety
All Ceramabind™ products are water-based materials that can be washed from the skin, in the uncured state, with mild soap and warm water.; Prolonged skin contact should be avoided to prevent irritation.; If any material contacts the eyes, flush continuously with water or neutralizing solutions, then consult a physician immediately.
- Carrier
- Water
- Markets
- Adhesives & Sealants
- Paints & Coatings
- Storage
Storage Unopened containers have a six-month shelf life when stored at room temperature.; Make sure opened containers are capped securely to prevent evaporation.; Place a plastic film in between the cap and container to prevent air leakage.; Store containers between 45ºF and 95ºF.
- Cure
- Air Dry
- Heat Cure
- Technology
- CASE Ingredients
- Application and Mixing
Liquid binder-to-powder weight ratios of 4:1 to 1:1 are recommended when formulating adhesives, coatings and pastes.; Powder binder (875) to filler ratio of 1:4 is recommended.; Blend powder slowly into binder until desired viscosity is achieved.; Vacuum degas as required to reduce entrapped air.; Apply the mixture to clean surfaces.; Extremely smooth surfaces are difficult to wet and should be sandblasted, etched, or slightly oxidized wherever possible.; Porous substrates tend to absorb and separate the binder from the powder; these substrates should be pre-coated with the binder only before applying the mixture.
- Compatible Substrates and Surfaces
- Ceramic
- Metal
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit |
|---|---|---|
| pH Value | 10.7 | — |
| Density | 1.41 | g/cc |
| Viscosity | 370.0 | cP |
| Solids Content by Weight | 40.0 | % |
| Temperature Resistance | 3000.0 | ºF |