VINNAPAS® 5010 N (GER)
- Chemical Family
- Vinyl Acetate Ethylene (VAE) Copolymer
VINNAPAS® 5010 N (GER) is a multi-purpose dispersible polymer powder for dry mix mortars, specifically suited for tile adhesives, renders, and trowelling compounds. It is based on a hard copolymer of vinylacetate and ethylene and belongs to the product class VINNAPAS® N, which means that it has a neutral effect on rheology and provides the basic properties of adhesion and flexibility, giving a high degree of formulation freedom. VINNAPAS® 5010 N (GER) is part of our standard range, offering the best-in-class solution for a wide variety of applications.
Properties
- Physical Form
- Powder
Product families
- Mortar & Gypsum Additives
Other characteristics
- Brand
- VINNAPAS
- Features
Abrasion Resistance, Anti-Blocking, Excellent Adhesion, Improved Flexibility, Improved Workability
- Markets
- Building & Construction
- Appearance
- White to light beige powder
- Properties
VINNAPAS® 5010 N (GER) is a copolymer powder of vinyl acetate and ethylene and is dispersible in water.; Compounds modified with VINNAPAS® 5010 N (GER) exhibit improved adhesion, flexural strength, deformability, abrasion resistance and are easier to process. Leveling, thixotropy and water retention are essentially unaffected.; The product is ideal for use in combination with other mortar additives intended to enhance specific properties.; VINNAPAS® 5010 N (GER) contains a fine mineral filler as an antiblocking agent.; It is produced without the addition of organic solvents, plasticizers and film-forming agents.; VINNAPAS® 5010 N (GER) has no effect on rheological properties and is a general-purpose powder in the upper Tg range. It is eminently suitable for formulating compounds of high ultimate strength and low emissions.
- Shelf LIfe
- 6 Months
- Technology
- Industrial Additives & Materials
- Dispersible In
- Water
- Packaging Type
- Bags
- Bulk
- Super Sacks
- Labeling Claims
- Plasticizer-free
- Specific Features
- Adhesion on critical surfaces
- Application Details
For the production of ready-mixed dry mortars, such as adhesives and patching compounds, blend VINNAPAS® 5010 N (GER) with the other dry ingredients in appropriate equipment. Temperatures should not be allowed to rise excessively during mixing because otherwise the dispersible polymer powder could agglomerate by virtue of its thermoplastic properties. The mortar is prepared for use by adding the recommended amount of water and mixing mechanically or by hand. Since hand mixing generates little shear force, we recommend allowing the fresh mortar to slake for 5 minutes and then stirring it again. This is usually unnecessary where mechanical mixers are employed.
- Storage Information
During storage, protect the product from contact with moisture. Prolonged storage at temperatures above 30°C, especially in combination with pressure, humidity or exposure to sunlight, may result in blocking. Carefully seal any open containers and store them under suitable conditions. We recommend storing the product in a warehouse that provides cool and dry conditions. Do not store the product for more than six months, starting from the date at which it was received.
Technical data
Table 1 of 2
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Minimum Film Forming Temperature | 4 | °C | DIN ISO 2115 |
| Protective Colloid (Emulsifier System) | Polyvinyl alcohol | — | — |
Table 2 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Ash Content (at 1000°C) | max. 13 | % | Specific Method |
| Bulk Density | 490 - 590 | kg/m³ | DIN EN ISO 60 |
| Particle Size (min. 400µm) | max. 4 | % | DIN EN ISO 4610 |
| Solids Content | min. 98 | % | DIN EN ISO 3251 |