VINNAPAS® 510 ED
- Chemical Family
- Vinyl Acetate Ethylene (VAE) Copolymer
VINNAPAS® 510 ED is a polymer dispersion based on vinyl acetate and ethylene. It is produced without the use of organic solvents, plasticizers, or formaldehyde donors. The residual monomer content of the dispersion is below 1000 ppm. VINNAPAS® 510 ED offers several advantages in building chemical applications as well as in general adhesives. To achieve optimum weathering resistance, opaque pigments should be used to ensure adequate pigmentation.
Properties
- Physical Form
- Dispersion
Product families
Industrial — Chemical & Industrial Manufacturing
- Resin Manufacturing
Other characteristics
- Brand
- VINNAPAS
- Features
Good Pigmentability, Improved Flexibility, Improved Flexural Strength, Water Resistance, Weather Resistant
- Functions
- Binder & Resin
- Markets
- Industrial
- Shelf LIfe
- 9 Months
- Technology
- CASE Ingredients
- Industrial Additives & Materials
- Packaging Type
- Drums
- Totes (IBC)
- Labeling Claims
- Plasticizer-free
Technical data
Table 1 of 2
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Appearance of the Dispersion Film | Slight hazy glossy | — | Visual |
| Content Residual Monomer (Vinyl Acetate) | max. 1000 | ppm | Specific method |
| Density (at 20°C) | approx. 1.07 | g/cm³ | Specific method |
| Filler and Pigment Compatibility | Very good | — | — |
| Glass Transition Temperature | approx. 19 | °C | Specific method |
| Minimum Film Forming Temperature | 5 | °C | Specific method |
| Predominant Particle Size | approx. 1 | µm | Specific method |
| Protective Colloid (Emulsifier System) | Polyvinyl alcohol | — | — |
Table 2 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (at 25°C) | 1500 - 2500 | mPa·s | Specific method |
| pH | 4.0 - 6.0 | — | Specific method |
| Solids Content | 54 - 56 | % | Specific method |