VINNAPAS® CEF 52
VINNAPAS® CEF 52 is a dispersion of a vinyl chloride, ethylene, and vinyl ester terpolymer. It can be used as a binder for coating systems containing an opacifying pigment, such as polymer-modified plasters. The special composition and manufacturing technology mean that VINNAPAS® CEF 52 can be used to formulate very hydrophobic products.
Properties
- Physical Form
- Dispersion
Product families
CASE Ingredients — Resins & Binders
- Other Resins & Binders
Other characteristics
- Brand
- VINNAPAS
- End Uses
- Base Coat
- Features
Abrasion Resistance, Alkali Resistance, Flame Resistance, High Tensile Strength, Improves Adhesion, Saponification Resistance, Water Resistance
- Glass Transition Temperature (Tg)
- 14.0 - 14.0 °C
- Markets
- Building & Construction
- Industrial
- Paints & Coatings
- Properties
- Excellent water resistance
- Very good alkaline resistance
- Very good flameresistance
- Good compatibility with cement
- Shelf LIfe
- 6 Months
- Coating Type
- Base Coat
- Technology
- CASE Ingredients
Technical data
Table 1 of 2
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Appearance of the Dispersion Film | Clear glossy | — | Visual |
| Density | approx. 1.13 | g/cm³ | DIN EN ISO 2811-1 |
| Electrolyte Stability | Very good | — | Specific method |
| Elongation (at break) | approx. 450 | % | DIN EN ISO 527-3 |
| Filler and Pigment Compatibility | Very good | — | Specific method |
| Film Surface | Tack free | — | Specific method |
| Film-Forming Aids, Solvents, Plasticizers | 1.6 (fatty acid ester based on dispersion) | wt % | Specific method |
| Glass Transition Temperature | approx. 14 | °C | Specific method |
| Minimum Film Forming Temperature | approx. 7 | °C | DIN ISO 2115 |
| Predominant Particle Size | approx. 0.3 | µm | Specific method |
| Protective Colloid (Emulsifier System) | Ionic and Non-ionic surfactants | — | — |
| Tensile Strength | approx. 5.0 | N/mm² | DIN EN ISO 527-3 |
Table 2 of 2
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Dynamic Viscosity (at 23°C, Brookfield, spindle 4, 20 rpm) | 3000 - 8000 | mPa·s | DIN EN ISO 2555 |
| pH | 7 - 9 | — | DIN/ISO 976 |
| Solids Content | 59 - 61 | % | DIN EN ISO 3251 |