TOHMIDE 92
- CASE Ingredients Features
- Blocking ResistanceHeat ResistanceMulti-Substrate AdhesionOil ResistanceWater Resistance
- Chemical Family
- Polyamides
TOHMIDE 92 is fatty polyamide resin especially designed for the flexographic printing ink uses.One of the major characteristics of TOHMIDE 92 the high water resistance of the ink films based on this resin in spite of its good solubility in alcoholic solvents
Properties
- Physical Form
- Pellets
- Solid
Identification
- CASE Ingredients Functions
- Binder & Resin
Product families
Applications
- Flexography
Product Families
- Other Resins & Binders
Other characteristics
- Brand
- TOHMIDE
- End Uses
- Flexography Ink, Solventborne Ink
- Features
Blocking Resistance, Heat Resistance, Multi-Substrate Adhesion, Oil Resistance, Water Resistance
- Carrier
- Solvent-based
- Markets
- Printing & Packaging
- Appearance
- Brown Yellow Pellets
- Technology
- CASE Ingredients
- Packaging Type
- Bags
- Ink and Toner Type
- Flexography Ink
- Solventborne Ink
- Ink Formulation
Polyamide resin ：12.0 Parts by Weight; Phthalocyanineblue pigment ： 7.5; Nitrocellulose. "L-1/8 sec."(=30％ wetted by isopropanol) ： 3.0; Isopropanol ：27.0; Ethyl-acetate ： 1.5; Ethyleneglyool - monoethylether ： 1.5; Total ：52.5; About formulation was prepared to ink by a ball milling.
- INK TEST -Testing Conditions
Water resistance ：Each sample ink was printed onto an treated polyethylene film. The sample print was then immersed in tap water for 16 hours at room temperature. Afterwards the ink film was subjected to "Scotch Tape-Test" with the excess water wiped off.; Oil resistance ：Margarine was coated onto the sample prints of treated polyethylene substrate, and 16 hours later, "Scotch Tape-Test" was conducted.; Heat (-sealing) resistance：Heat-sealing bar, with the load of 1 kgr./㎝ 2 , was applied onto the sample ink film on treated polypropylene for one second.; Anti blocking test ：The sample inks were printed on treated polyethylene film of an aluminum foil. The ink films were then subjected to static load of 1 kgr/㎝ 2 , for 16 hours under a condition of 50℃, R/H=50％
Technical data
Table 1 of 1
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Softening Point | 120±5 | Ball and Ring /℃ |
| Viscosity (Gardner-Holdt /25℃) | *C ~ F | — |
| Acid Value | max. 7 | mg KOH/g |
| Amine Value | max. 5 | mgKOH/g |