PRF Composite Materials RP801
- Chemical Family
- Epoxy & Epoxy Derivatives
PRF Composite Materials RP801 is an epoxy tooling prepreg system capable of withstanding temperatures up to 190°C after full post cure. RP801 is available in carbon and glass woven fabrics from 200 - 800 g/m2 impregnated with epoxy resin. RP-801 prepreg allows high quality tooling laminates to be produced directly from a low temperature master model permitting a wide choice of master model materials. Using a low temperature vacuum bag and autoclave process for inital cure, the tool laminate can then be demoulded for freestanding post cure.
Properties
- Physical Form
- Fabric
Product families
Applications
- Consumer Goods — Sports & Recreation
- Interior
- Tooling & Moldmaking
- Aerospace & Aviation
Product Families
- Thermoset Prepregs
Other characteristics
- Functions
- Prepreg
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Prepreg Processing, Vacuum Bagging
- Reinforcement Material
- Carbon Fibers, Glass Fibers
- Carbon Fibers
- Glass Fibers
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Cure Cycle
Preferred initial cure can be either of the following: 60°C for 8 hours 70°C for 4 hours Heat ramp up rate: 1.0°C/minute up to temperature, under 7 bar pressure and >0.9 bar vacuum. Cool naturally. Tooling can be removed from the master after this cure. For post cure, the tool must rest on a level surface to prevent possible deformation. The recommended post cure cycle is as follows: • From initial cure temperature, ramp up at 1°C per minute up to 170°C and cure for >2.5 hours, then cool naturally. This will provide a Tg >170°C (DSC). • Post cure > 4h @ 170°C provides a Tg of 190°C (DSC).
- Shelf LIfe
- Storage Temperature
- Technology
- Composite Materials
- Material Features
- Good Surface Finish
- Reinforcement Form
- Woven Fabric
- Benefits and Features
- Initial cure from 60°C to 70°C
- Post cure: 170°C
- Autoclave processing
- Excellent surface finish
- Composite Materials Functions
- Prepreg
- Composites Processing Methods
- Prepreg Processing
- Vacuum Bagging
Technical data
Table 1 of 2
1 row| Characteristic | Value | Unit |
|---|---|---|
| Thermogravimetry (DSC) | 190 | °C |
Table 2 of 2
1 row| Characteristic | Value | Unit |
|---|---|---|
| Cure Temperature | 60–180 | °C |