PRF Composite Materials RP570
- Chemical Family
- Epoxy & Epoxy Derivatives
PRF Composite Materials RP570 is a high performance formulated epoxy resin system with rapid Tg development enabling extremely short process times and excellent esthetic finish. A press tool held at constant temperature of 140°C can produce a part every 4 minutes ready for painting. RP-570 can be supplied on a variety of woven fabrics.
Properties
- Physical Form
- Fabric
Product families
Applications
Automotive & Transportation — Automotive
- Other Automotive Applications
Automotive & Transportation — Transportation
- Aerospace & Aviation
- Marine
Product Families
Composite Materials — Prepregs & Molding Compounds
- Thermoset Prepregs
Other characteristics
- Functions
- Prepreg
- Polymer Name
- Epoxy Resins & Compounds
- Processing Methods
- Compression Molding
- Pressing
- Reinforcement Material
- Carbon Fibers
- Fibre
- Carbon
- Markets
- Automotive & Transportation
- Cure Cycle
Carefully place prepreg preforms in 140°C preheated hot tool. Close tool under 10 bar pressure and maintain 140°C temperature. Release pressure after 4 minutes and remove cured part.
- Fibre Type
- TR30s-3K
- Technology
- Composite Materials
- Material Features
- Good Surface Finish
- Reinforcement Form
- Woven Fabric
- Storage Condition
- 6 months at -18°C
- 30 days at 23°C
- Benefits and Features
• Cures and is demouldable in 4 minutes at 140°C • Tg >140°C • Excellent surface finish • No thermal cycling of tools required • Fast Tg development • Can be preformed
- Composite Materials Functions
- Prepreg
- Composites Processing Methods
- Compression Molding
Technical data
Table 1 of 2
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Fabric Weave Style | Twill 2/2 | — | — |
| Fabric Weight | 245 | g/m2 | — |
| Resin Content | 42 | % | — |
| Fibre Volume Fraction | 48 | % | — |
| Thermogravimetry (Dsc) | 140 | °C | — |
| Thermogravimetry (Dma Onset) | 131 | °C | — |
| Thermogravimetry (Dma Peak) | 155 | °C | — |
| Tensile Strength | 840.4 | MPa | ASTM D3039 |
| Tensile Modulus | 63.1 | GPa | ASTM D3039 |
| Interlaminar Shear Strength (Ilss) | 66.9 | MPa | EN ISO 14130 |
| Flexural Strength | 948.2 | MPa | EN ISO 178 |
Table 2 of 2
1 row| Characteristic | Value | Unit |
|---|---|---|
| Cure Temperature | 140 | °C |