Taita Chemical 1003
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
TAITALAC 1003 ABS Resin is Acrylonitrile Butadiene Styrene (ABS) Resin and it is used in Electrical appliances, Large complex shaped products, precision molding, Houseware, 3C product case and office equipment / OA supplies.
Properties
- Physical Form
- Pellets
- Solid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Stationery
- Art & Office Supplies
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Electrical & Electronics — Parts & Components
- Housings & Enclosures
Product Families
Plastics — Basic Thermoplastics
- Styrenics
Other characteristics
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Processing Methods
- Injection Molding
- Color
- White
- Markets
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Characteristic
- Injection
- High impact
- High flow for process
- High productivity
- Material Features
- High Flow
- High Impact Performance
- High Productivity
- Certifications and Compliance
Directive 2011/65/EC amended through EU/2015/863 (RoHS); UL 94
- Plastics and Elastomers End Uses
- Appliances
- Housewares
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Elongation at Break (23°C, 5 mm/min) | 40.0 | % | ASTMD638 |
| Flexural Modulus (23°C, 2.8 mm/min) | 25000.0 | kg/cm2 | ASTMD790 |
| Flexural Yield (23°C, 2.8 mm/min) | 670.0 | kg/cm2 | ASTMD790 |
| Izod Impact Strength (23°C, 1/4” Notched) | 22.0 | kg-cm/cm | ASTMD256 |
| Izod Impact Strength (23°C, 1/8” Notched) | 24.0 | kg-cm/cm | ASTMD256 |
| Tensile Strength at Break (23°C, 5 mm/min) | 330.0 | kg/cm2 | ASTMD638 |
| Tensile Strength at Yield (23°C, 5 mm/min) | 370.0 | kg/cm2 | ASTMD638 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption Equilibrium (23°C/50% RH) | max. 0.3 | wt% | ASTMD570 |
| Mold Shrinkage (60×60×2mm SFlow) | max. 0.4 | wt% | ASTMD955 |
| Rockwell Hardness (23°C, R-scale) | 107.0 | R-scale | ASTMD785 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Distortion Temperature (Unannealing 1.8MPa) | 85.0 | °C | ASTMD648 |
| RTI Elec (1.7 mm) | 60.0 | — | UL 746 |
| RTI Imp (1.7 mm) | 60.0 | — | UL 746 |
| RTI Str (1.7 mm) | 60.0 | — | UL 746 |
| Vicat Softening Temperature (50°C/hr , 1 kg load) | 102.0 | °C | ASTMD1525 |
Table 4 of 7
3 rows| Characteristic | Value | Method |
|---|---|---|
| High Amp Arc lgnition (1.7 mm) | PLC 3 | UL 746 |
| High Voltage Arc Tracking Rate | PLC 1 | UL 746 |
| Hot-Wire Ignition (1.7 mm) | PLC 5 | UL 746 |
Table 5 of 7
2 rows| Characteristic | Value | Method |
|---|---|---|
| Flame Rating (1.7 mm, ALL) | HB | UL 94 |
| Flame Rating (1.7 mm, ALL) | HB 75 | IEC 60695-11-10,-20 |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 50 - 70 | psi(Mpa) |
| Drying Temperature | 80 - 85 | °C |
| Drying Time | 2.0 - 4.0 | hr |
| Front Zone | 180 - 210 | °C |
| Injection Pressure | Low To Moderate | — |
| Injection Speed | Low To Moderate | — |
| Melt Zone | 170 - 180 | °C |
| Middle Zone | 190 - 220 | °C |
| Mold Temperature | 40 - 70 | °C |
| Nozzle | 200 - 230 | °C |
| Rear Zone | 180 - 210 | °C |
| Screw Speed | 30 - 100 | rpm |
Table 7 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Volume Rate (200°C, 5kg load) | 3.5 | g/10min | ASTM D1238 |
| Melt Volume Rate (220°C, 10kg load) | 35.0 | g/10min | ASTM D1238 |
| Specific Gravity (23°C) | 1.03 | g/cm3 | ASTM D792 |